Role of Macrodiols in the Synthesis and Thermo-Mechanical Behavior of Anti-Tack Water Borne Polyurethane Dispersions

Nadia Akram,Muhammad Saeed,Muhammad Usman

DOI: https://doi.org/10.3390/polym14030572

IF: 5

2022-01-31

Polymers

Abstract:The texture and molecular weight of polymer drastically affect the adhesion or tack strength. Waterborne polyurethane dispersions (WBPU) have been prepared using two different macrodiols of hydroxyl terminated polybutadiene (HTPB; Mn = 2912 g/mol−1) and four compositions of Polypropylene glycol (PPG Mn = 425, 1000, 2000, 2700 g/mol−1). The contents of the macrodiols have been varied using HTPB as 5, 10 and 15 mol%. The prepolymer of HTPB and Poly propylene glycol (PPG) have been developed using 4,4-Methylene bis(cyclohexyl isocyanate) (H12MDI) which is extended using 1, 4 butanediol (BD) followed by the dispersion of polymers in deionized water. Fourier Transform Infra-red spectroscopy (FTIR) is used to confirm the desired PU linkage. The probe tack graphs for tack analysis have not shown any plateau indicating absence of fibrillation. Two different values of glass transition temperature (Tg) have been observed for each dispersion using Differential Scanning Calorimetry(DSC). Storage modulus (E′) up to 3.97 MPa and (tanδ/E′) from 0.01–0.30 MPa−1 has been observed via Dynamic Mechanical Analysis (DMA). Introducing the HTPB has resulted in a decrease in the values of (tanδ/E′). No adhesion favorable parameters have been retrieved, indicating the molar variation a key factor in the development of anti-tack dispersions.

polymer science