Controllable Blading Interdiffusion of Formamidinium Iodide on Thermal Evaporated Scalable and Conformal Lead Iodide for Efficient Perovskite Solar Cells
Jun Fang,Dongxu Lin,Weixin Huang,Xin Wang,Huan Li,Sibo Li,Guanshui Xie,Daozeng Wang,Longbin Qiu
DOI: https://doi.org/10.1016/j.jallcom.2023.170255
IF: 6.2
2023-04-26
Journal of Alloys and Compounds
Abstract:Organic-inorganic perovskite solar cells with a rapid improving performance have attracted a broad interest, which are mainly fabricated by either one step antisolvent or sequential two-step spin coating process. The sequential two-step coating process has a fine controllability by separating the deposition of PbI 2 and organic salt like formamidinium iodide. However, the spin coating has issues such as the use of toxic solvents, a high solution waste ratio and is not suitable for large-area and textured surface. The developed sequential two-step process combining the thermal evaporation of scalable and conformal PbI 2 and a blading process of organic salt is expected for the formation of high-quality perovskite with a high uniformity and conformability. However, the device performance is inferior to the two-step solution coating process. Here we systematically investigated the structure and morphology difference of the PbI 2 that deposited by solution coating process and thermal evaporation process, and its effect on perovskite layer quality and device performance. The spin coated solvent coordinated PbI 2 formed a porous structure, which is beneficial for organic salt penetration. In contrast, evaporated PbI 2 is compact with a smooth surface, and may lead to unwanted 2D structures or un-completed conversion when reacted with organic ammonium salt. A temperature-assisted crystal growth is developed to modulate the crystal growth and a superior perovskite film morphology was obtained from thermal evaporated PbI 2 . Consequently, a champion efficiency of 19.8% was realized, which is among the highest values for perovskite solar cells prepared by sequential two-step thermal evaporation of PbI 2 and blading of organic salts.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering