Abstract:Amphiphilic azo polymers with different azo chromophores and degree of functionalization (DF) were synthesized, and colloidal spheres of the polymers were prepared by gradual hydrophobic aggregation in selective solvents. To obtain suspensions of colloidal spheres, the required amounts of water were added into the THF solutions at a certain stirring rate. As the water content reached ca. 70 vol%, an excess of water was added into the suspensions to "quench" the formed structures. The obtained suspensions of colloidal spheres were sealed after THF was completely volatilized and were characterized by DLS and UV-Vis spectroscopy. The size and size-distribution of colloidal spheres were measured by using a DLS/SLS-5022F laser light scattering apparatus. Before the measurement, the sample was clarified by a 0.45 mu m Millipore filter to remove dust, and all the DLS measurements were carried out with 90 degrees scattering angle. UV-Vis spectroscopy was used to study the azo chromophore structure variation in the colloid formation process by measuring the parameters such as the trans-to-cis photoisomerization rate and the isomerization degree at the photostationary state. In the photoresponse experiments, the sample was irradiated by a 365 nm UV light source, and the light intensity was 7000 mV/cm(2) at a distance of 38 cm and 21000 mV/cm(2) at a distance of 5 cm. respectively. In our experiment. the sample was 15 cm away from the UV light, and the temperature of the environment was 30 degrees C. The influences of molecular structure and preparation conditions on the size and photoresponsive properties of the colloidal spheres were studied in some detail. The result shows that the functional group type and DF as well as the preparation conditions (initial polymer concentration, the rate of water addition, etc.) have significant effects on the size and photoresponsive properties of the colloidal spheres. The size of colloidal spheres increases with the increase of DF and initial concentration, but decreases with the increase of the rate of water addition. The photoinduced isomerization rate of poly {2-[4-(4-ethoxyphenylazo)phenoxy] ethyl acrylate-co-acrylic acid} (PEAPE) colloids is higher than that of poly {2-[4-(4-cyanophenylazo) phenoxyl ethyl acrylate-co-acrylic acid} (PCNPE) colloids. The PEAPE colloids with higher DF show a slower photoisomerization rate. The photoinduced isomerization rate of the colloids decreases with the increase of initial concentration and the decrease of the rate of water addition. The possible mechanism for the influence is also discussed based on thermodynamics and kinetics consideration. It is believed that the colloidal spheres form through a self-assembling process controlled by the dynamic conditions. For high initial concentration and slow water dropping rate, more polymer chains tend to aggregate on the compact cores formed from the most hydrophobic chains as the water content is above the critical water content (CWC). Moreover, the polymeric chains had chance to rearrange themselves to form stable and compact structures due to the slow rate of water addition. On the other hand, as the rate of water addition increased I the polymeric chains attached to the cores were quickly "frozen" before they could completely adjust their conformations. Also, they could form new less compact cores so as to weaken the continuous aggregation probability. As a result, the formed aggregates had loose structures, and the photoinduced isomerization rate was relatively fast.

Effect of disperse dye on the preparation of poly(vinyl acetate)/poly(vinyl alcohol)/disperse dye composite microspheres

Synergetic Effect of a Reactive Compatibilizer and Organo-montmorillonite on the Dispersion of Polyamide 6 /Polydimethylsilicone Blend with a High Viscosity Ratio

Morphology and blowing agent encapsulation efficiency of vinylidene chloride copolymer microspheres synthesized by suspension polymerization in the presence of a blowing agent

Colorating and Mechanical Performance of Low-Density Polyethylene (Ldpe)/dye-Loaded Shell Powder (DPSP) Composites

Preparation, Characterization And Filling Effect Study Of Dye-Loaded Shell Powder On The Properties Of Ldpe Composite

Particle Diameter and Morphology of Vinylidene Chloride-Vinyl Chloride Suspension Copolymer

Influences of individual and composed poly(vinyl alcohol) suspending agents on particle morphology of suspension poly(vinyl chloride) resin

Influence of Suspended Emulsion Polymerization Conditions on Particle Characteristics of Polyvinyl Chloride Resin

Study on the dispersion mechanism of the polycarboxylic acid dispersant for disperse dyes

The Effects of Particle Size and Distribution of Disperse Dye on the Dyeing Performance of PLA Blended Fabric

Characteristics of Vinylidene Chloride-Vinyl Chloride Copolymer Resin Particles

Synthesis, Drug Absoprtion and Release Properties of Poly(methyl Methacrylate)/ Poly( 2-Hydroxyethyl Methacrylate) Composite Microspheres

Mechanical and Thermal Properties of Low Density Polyethylene Composites Filled with Dye-Loaded Shell Powder

Synthesis and Dye Adsorption Dynamics of Chitosan–Polyvinylpolypyrrolidone (PVPP) Composite

Filling And Coloring Effect Of Pearl Shell Powder And Dye-Loaded Pearl Shell Powder On Polypropylene

Red Disperse Azo Dye Side Chains Influence on Polyethylene Terephthalate Dyeing Performances in Supercritical Carbon Dioxide Media

Effects of Dye Addition on the Rheological Properties of Aqueous Polymer Solutions

Study on the Compatibility of Pa6/Lldpe/Nano-Sized Copolymer Microspheres Composites

Structured polymer dispersant for efficient phthalocyanine blue dispersion and color paste preparation

INFLUENCES OF STRUCTURE AND PREPARATION CONDITIONS ON SIZE AND PHOTORESPONSIVE PROPERTIES OF AMPHIPHILIC AZO POLYMER COLLOIDAL SPHERES

Synthesis of Narrow Disperse Crosslinked Poly(Divinylbenzene) Microspheres in Acetic Acid Via Precipitation Polymerization