Abstract:The mechanical properties and thermal conductivity of Al–Si–Fe castings must meet high requirements in the automobile, aerospace, and communication fields. Traditional high-pressure diecasting (HPDC) castings often have dendritic structures and pore defects that deteriorate their overall performance. Therefore, an advanced rheo-diecasting (RDC) technique assisted by a vibrating contraction sloping plate was proposed to address this problem. However, the process optimization strategy, microstructural evolution, and performance improvement mechanisms remain unclear. The influence of the injection velocity on the microstructure, mechanical properties, and thermal conductivity of the RDC tensile specimens was first investigated. A high-performance cover plate was fabricated via RDC using an optimized injection velocity. The results showed that when the injection velocity increased to 2.8 m/s, the porosity decreased to a minimum value, and the mechanical performance and thermal conductivity of the RDC tensile specimens reached their maximum values. Furthermore, spherical eutectic Si phases and nanosized Mg 2 Si precipitates for the RDC cover plate were observed after T6 heat treatment, which further improved the mechanical properties and thermal conductivity owing to Orowan strengthening and decreased lattice distortion, respectively. The ultimate tensile strength, yield strength, elongation, and thermal conductivity for the RDC cover plate were 358.2 MPa, 279.9 MPa, 12.5%, and 180.72 W/(m·K), respectively, which were higher than that of reported similar alloys. From engineering perspectives, this study had the application value for produce of high-quality RDC castings.

A Study on the Effect of Insulating Sleeve on Solidification Characteristics of A356 Aluminum Alloy

A Study on the Effect of Insulating Sleeve on Solidification Characteristics of A356 Aluminum Alloy

On the Size Effects in Micro/meso Semisolid Extrusion–forging of A356 Aluminum Alloy

Numerical Simulation and Experimental Investigation of Microstructure Evolution and Flow Behavior in the Rheological Squeeze Casting Process of A356 Alloy

A New Technology to Improve the Elongation of A356 Alloy

The Effect of Initial Microstructure of A356 Alloys on the Mechanical Behavior in the Semisolid State

Experimental Studies on Rheocasting Processing of A356 Alloy

Effect of Solidification Rates at Sand Casting on the Mechanical Joinability of a Cast Aluminium Alloy

Rheologic Properties of Aluminum Alloy A356 Bille ts Produced by Semisolid Continuous Casting Process

Experimental Investigation and Numerical Simulation of the Fluidity of A356 Aluminum Alloy

Solidification behavior and enhanced properties of semi-solid Al–8Si–0.5Fe alloys fabricated by rheo-diecasting

Numerical Simulation of Lost-Foam Casting for Key Components of A356 Aluminum Alloy in New Energy Vehicles

Enhanced comprehensive performance via alloying and rheo-diecasting in a semi-solid Al–Si–Fe–Mg–Cu–Sr alloy

New technique for preparing A356 alloy semisolid slurry and its rheo-diecast microstructure and properties

To Improve Robustness of Mechanical Properties of Semi-Solid Cast A356 Alloy Using Taguchi Design Method

Towards high performance Al–Si–Fe alloy castings via rheo-diecasting: Effect of injection velocity and heat treatment on microstructure evolution and property

Investigation of Properties in Magnesium Alloy Thin Plates after Die Casting Processes

Numerical Simulation of Semi-Solid Die-Casting Process of Automobile Aluminum Alloy Part

An Investigation into Aluminum–aluminum Bimetal Fabrication by Squeeze Casting

Numerical Simulation and Experimental Study on Semi-solid Forming Process of 319s Aluminum Alloy Test Bar

The comparison of intensive riser cooling of castings after solidification in three classic metals