Abstract:The high content of iron in ilmenite ore poses a great challenge, particularly in the synthesis of titanium-containing products due to high susceptibility of iron (Fe) to corrosion. Direct leaching of ilmenite ore in hydrochloric acid (HCl) encouraging Fe dissolution was investigated. The influence of variable parameters, the use of additives, and the addition of metallic iron powder were studied to establish the optimum leaching parameters. The results showed that ilmenite with the particle size distribution of +150 μm yielded better efficiencies when leaching was performed with an acid concentration of 7.5 M and a solid-to-acid ratio of 1:10 at 90 °C. An agitation speed of 450 rpm yielded a superior Fe extraction of about 92.32% and a 2.40% titanium (Ti) loss. The addition of both metallic Fe and the MgSO4 additive significantly enhanced Fe dissolution and decreased Ti recovery in a leach solution. It was found that leaching under optimum conditions produced a solid residue with 1.37% Fe impurity while 98.63% was extracted. The leached residue was comprised of 91.4% TiO2 rutile phase and contained a high content of the ilmenite FeTiO3 (4.37%) and SiO2 (2.23%) impurities, while Al2O3, MgO, MnO2, CaO, V2O5, MnO2, and Cr2O3 were below 0.13%. The high TiO2 content in the leached residue makes it suitable for use as feed in the production of synthetic rutile. The leaching kinetics of Fe dissolution was found to conform to the shrinking core model, where diffusion through the product layer is rate controlling. The calculated activation energy according to the Arrhenius equation was 19.13 kJ/mol.

Thermodynamic Consideration of the Removal of Iron from Titanium Ore by Selective Chlorination

Removal of Iron from Titanium Ore through Selective Chlorination Using Magnesium Chloride

Production of Titanium Dioxide Directly from Titanium Ore through Selective Chlorination Using Titanium Tetrachloride

Production of High-Grade Titanium Dioxide Directly from Titanium Ore Using Titanium Scrap and Iron Chloride Waste

Thermodynamic Analysis of Titanium Removal from Molten iron Smelted with Large Amounts of Sodium Additives

Recovery of titanium metal scrap by utilizing chloride wastes

Reaction-Mediator-Based Chlorination for the Recycling of Titanium Metal Scrap Utilizing Chloride Waste

Comparison of Methods for Electrochemical Iron Removal from Titanium Ores

Solvent Extraction of Titanium from Ilmenite Hydrochloric Acid Leachate: Optimization and Investigation of Extraction Reactions of All Contained Metal Ions

Thermodynamics on the reaction of carbochlorination of titania for getting titanium tetrachloride

Chlorination Behavior of Low-Grade Titanium Slag in AlCl3-NaCl Molten Salt

Enhancement of the Low Temperature Chlorination of Ilmenite with CCl4 by Adding Cl2

Effective Deoxidation Process of Titanium Scrap Using MgCl2 Molten Salt Electrolytic

Selective Extraction of Valuable and Critical Metals in Cassiterite Concentrate by Dry Chlorination, Part I: Thermodynamic and Modelling Perspective

Kinetics of Iron Removal From Ti-Extraction Blast Furnace Slag by Chlorination Calcination

Ilmenite Chlorination: Usage of Gaseous Carbon Tetrachloride at Relatively Lower Temperatures

Removal of chloride impurities from titanium sponge by vacuum distillation

Effect of NH4Cl on the rusting leaching behavior of metallic phase of iron in reduced ilmenite during TiO2 purification: An electrochemical and density-functional theory study

Iron Extraction from South African Ilmenite Concentrate Leaching by Hydrochloric Acid (HCl) in the Presence of Reductant (Metallic Fe) and Additive (MgSO4)

The selective chlorination of iron from llmenite ore by CO-Cl2 mixtures: Part I. intrinsic kinetics