Abstract:The outer wall of the ethylene cracking furnace tube is subjected to thermal radiation, while the inside of the tube has a high carbon potential and low oxygen pressure. Small punch test (SPT) technique can be used to sample the outer surface of the furnace tube. However, since the complex conditions of the inner and outer surfaces of the tube, the representativeness of the outer surface sampling needs to be studied. Therefore, in order to investigate the damage situation of the furnace tube in the radiation section of the in-service ethylene cracking furnace made of 25Cr35NiNb alloy along the thickness direction of the tube, microstructure and SPT were used to compare the in-service 7-year-old furnace tube with a new furnace tube, and the feasibility of using SPT instead of the uniaxial test was explored. The results showed that the microstructure, chemical elements, and hardness of the in-service furnace tube varied at different positions along the thickness direction compared with the new furnace tube. The SPT at room temperature revealed that the performance degradation at the inner and outer surfaces was more serious than that at the middle. The small punch creep test (SPCT) found that the outer surface had a shorter fracture time than the inner surface at the same temperature and load, indicating that the outer surface was more severely damaged than the inner surface. The SPT showed consistency with the uniaxial test in mechanical properties and fracture morphology. The results of this study provide strong technical support for future assessment of damage and remaining life prediction of inservice ethylene cracking furnace tubes based on the SPT technique.

D123 Damage Assessment of Highly Aged Thermal Power Boiler Tubes by TEM-Size SP Creep Test

D122 SP Creep properties of Aged Boiler Tube Used in Thermal Power Station

D121 Application of Miniature Creep Test to the Assess ment of Creep Damage in Aged Thermal Power Boiler Tubes

Creep-fatigue Endurance of a Superheater Tube Plate under Non-Isothermal Loading and Multi-Dwell Condition

Evaluation of creep damage of the steam pipelines with high temperature and high pressure

Multi-axial Stress Creep Testing Methods for High Temperature Materials

Creep Behaviors Calculated by Varying Material Constants Obtained from Different Stress Regions for a Closed-End P91 Pipe

Residual Life Assessment of In-Service High Temperature Components by Small Punch Creep Test

Microstructure evolution and performance evaluation of T122 steel before and after service

In-Situ Synchrotron X-Ray Study Of The Elevated Temperature Deformation Response Of Ss 316l Pressurized Creep Tubes

Experimental Investigation on Creep Behaviors and Life Prediction Across Phase-Transformation of Thermal Aged 16MND5 Steel

Structural and Mechanical Characterization of Service Exposed 2.25Cr–1Mo Steel

Creep Damage Assessment of Ex-Service 12% Cr Power Plant Steel Using Digital Image Correlation and Quantitative Microstructural Evaluation

Damage Analysis of In-Service Ethylene Cracking Furnace Tubes Using Small Punch Test

Expansion of High Temperature Creep Test Data for Failure Evaluation of BWR Lower Head in Severe Accident

Safety assessment method for defective structures in creep regime

Small punch test for investigating circumferential creep in cladding tubes

TDFAD-BASED "THREE-LEVELS" ASSESSMENT METHOD FOR HIGH TEMPERATURE DEFECTS

Integrity Assessment of a 3D Tubeplate Using the Linear Matching Method. Part 2: Creep Relaxation and Reverse Plasticity

Analysis of the Creep Mechanism of Low-Alloy Steel in Terms of Plastic Deformation

CREEP DEFORMATION ANALYSIS OF A PIPE SPECIMEN BASED ON CREEP DAMAGE EVALUATION METHOD