Abstract:Following a brief report on high-temperature superconductivity in B-doped Q-carbon [Bhaumik et al., ACS Nano 11(6), 5351–5357 (2017)], we present detailed structure-property correlations to understand the origin of superconductivity in strongly bonded lightweight materials and methods to further enhance the superconducting transition temperature (Tc). Nanosecond melting of carbon in a super undercooled state and rapid quenching result in a strongly bonded unique phase of B-doped Q-carbon. The temperature-dependent resistivity and magnetic susceptibility measurements demonstrate type II superconductivity in this material with a transition temperature of 36.0 ± 0.5 K and an upper critical field of 5.4 T at ∼0 K. It has also been shown that in B-doped Q-carbon, the upper critical magnetic field (Hc2(T)) follows Hc2(0) [1-(T/Tc)2.1] temperature dependence and is consistent with the Bardeen–Cooper–Schrieffer formalism. In the present study, B-doped Q-carbon thin films are formed on sapphire substrates by employing pulsed laser annealing (PLA) using a nanosecond excimer laser. This process involves the rapid quenching of highly undercooled melt of homogenously mixed B and C. Through the structure-property correlation measurements in B-doped Q-carbon, we estimate a higher electronic density of states near the Fermi level. Higher density of states near the Fermi-level along with higher Debye temperature and phonon frequency are responsible for the enhanced Tc. As a result of rapid melting and quenching, we can achieve 17.0 ± 1.0 or higher atomic % of B in the electrically active sites of Q-carbon which leads to the formation of shallow electronic states near the valence band maximum. From the critical current density versus field moments, the value of critical current density (Jc (2T)) in B-doped Q-carbon at 21 K is calculated as 4.3 × 107 A cm−2, which indicates that this novel material can be used for the persistent mode of operation in MRI and nuclear magnetic resonance applications. This discovery of high-temperature superconductivity in B-doped amorphous Q-carbon shows that the non-equilibrium synthesis technique using the super undercooling process can be used to fabricate materials with greatly enhanced physical properties.
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to explore a new type of high - temperature superconducting material - boron - doped Q - carbon (B - doped Q - carbon). Specifically, the researchers prepared this material through non - equilibrium synthesis techniques, such as the super - cooling process, and studied in detail the relationship between its structure and properties in order to understand the reasons for the emergence of superconductivity in this lightweight and strongly - bonded material and explore methods to further increase the superconducting transition temperature (\(T_c\)).
The research background includes:
1. **Superconductivity in carbon - based materials**: The pure carbon structure limits the achievement of a higher superconducting transition temperature due to the lack of strong electron - phonon coupling and a high electron state density near the Fermi level.
2. **Limitations of existing carbon - based superconductors**: For example, graphite intercalation compounds, single - walled carbon nanotubes, alkali - metal - doped fullerenes, boron - doped diamonds, etc., their superconducting transition temperatures are relatively low.
3. **Application of non - equilibrium synthesis techniques**: Through non - equilibrium synthesis techniques, such as pulsed - laser annealing (PLA), high - concentration doping beyond the thermodynamic solubility limit can be achieved, and thus materials with higher physical properties may be obtained.
The main contributions of the paper are:
- Successfully prepared boron - doped Q - carbon and verified its structure and composition through multiple characterization means (such as Raman spectroscopy, X - ray diffraction, X - ray photoelectron spectroscopy, scanning electron microscopy, etc.).
- Discovered that the superconducting transition temperature of boron - doped Q - carbon is 36.0 ± 0.5 K, which is higher than that of existing carbon - based superconducting materials (such as boron - doped diamonds).
- Through theoretical analysis and experimental data, explained the mechanism of the high superconducting transition temperature in boron - doped Q - carbon, including a higher electron state density near the Fermi level, a higher Debye temperature and phonon frequency.
In summary, this paper aims to prepare boron - doped Q - carbon through non - equilibrium synthesis techniques and, through detailed structure - property correlation studies, reveal its superconducting mechanism, providing theoretical and experimental bases for further increasing the superconducting transition temperature.