Effect of Carbon Doping on the Structure and Superconductivity in AlB$_{2}$-type (Mo$_{0.96}$ti$_{0.04}$)$_{0.8}$b$_{2}$

Wuzhang Yang,Guorui Xiao,Qinqing Zhu,Shijie Song,Guanghan Cao,Zhi Ren

DOI: https://doi.org/10.48550/arxiv.2302.14272

2023-01-01

Abstract:We report the effect of carbon doping in Ti-stabilized nonstoichiometric molybdenum diboride (Mo$_{0.96}$Ti$_{0.04}$)$_{0.8}$B$_{2}$, which exhibits bulk superconductivity below $T_{\rm c}$ = 7.0 K. It is found that (Mo$_{0.96}$Ti$_{0.04}$)$_{0.8}$(B$_{1-x}$C$_{x}$)$_{2}$ maintains the AlB$_{2}$-type phase with a uniform elemental distribution for $x$ = 0.12 and 0.16. The substitution of carbon for boron leads to a slight increase in $a$-axis, a remarkable reduction in $c$-axis, the formation of planar defects along the (100) crystallographic planes, and a shift of the B 1$s$ peaks towards higher binding energies. Contrary to (Mo$_{0.96}$Ti$_{0.04}$)$_{0.8}$B$_{2}$, however, no superconductivity is observed down to 1.8 K for the C-doped samples, which is ascribed to the electron filling of boron $\pi$ bands resulting from the carbon doping.