Intralayer Carbon Substitution in the MgB2 Superconductor

T. Takenobu,T. Ito,Dam H. Chi,K. Prassides,Y. Iwasa

DOI: https://doi.org/10.1103/PhysRevB.64.134513

2001-03-12

Abstract:We report that the ternary MgB2-xCx compounds adopt an isostructural AlB2-type hexagonal structure in a relatively small range of nominal carbon concentration, x<0.1. The lattice parameter a decreases almost linearly with increasing carbon content x, while the c parameter remains unchanged, indicating that carbon is exclusively substituted in the boron honeycomb layer without affecting the interlayer interactions. The superconducting transition temperature Tc, determined by magnetometry experiments, also decreases quasilinearly as a function of the carbon concentration. The structural and electronic behavior of MgB2-xCx displays a remarkable similarity with the isoelectronic Mg1-xAlxB2 despite the different substitution sites.

Superconductivity,Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the influence of carbon atom substitution for boron atom in MgB₂ superconductor (i.e., forming MgB₂₋ₓCₓ compound) on the material structure and superconducting properties. Specifically, the author focuses on the following aspects:

1. **Changes in crystal structure**: To study whether the crystal structure of MgB₂ changes after carbon substitution for boron, especially the changes in lattice parameters a and c.
2. **Changes in superconducting transition temperature (Tc)**: To explore the influence of carbon substitution on the superconducting transition temperature and analyze its variation law.
3. **Comparison with isoelectronic systems**: To compare the effect of carbon substitution with the Mg₁₋ₓAlₓB₂ system formed by aluminum substitution for magnesium, so as to reveal the influence of different substitution sites on the material properties.

### Main findings

- **Crystal structure**: As the carbon content x increases, the lattice parameter a decreases almost linearly, while the c parameter remains unchanged, indicating that carbon mainly substitutes for boron atoms in the boron layer without affecting the inter - layer interaction.

\[
a(x)=a_0 - k_a x
\]
\[
c(x)=c_0
\]

where \(a_0\) and \(c_0\) are the lattice parameters without doping, and \(k_a\) is a proportional constant related to the carbon concentration.

- **Superconducting transition temperature (Tc)**: Tc decreases quasi - linearly with the increase of carbon concentration x, and the decreasing rate is \(\frac{dT_c}{dx}=- 57\,\text{K}\).

\[
T_c(x)=T_{c0}-57x
\]

where \(T_{c0}\) is the superconducting transition temperature without doping.

- **Similarity with Mg₁₋ₓAlₓB₂**: Although the substitution sites are different, the structure and electronic behavior of MgB₂₋ₓCₓ show significant similarity with Mg₁₋ₓAlₓB₂, which indicates that the electronic structures of these two systems can be well described by the band theory, and Tc is controlled by the density of states at the Fermi level.

These results provide important clues for understanding the superconducting mechanism of MgB₂ and its derivatives, and lay the foundation for further research on the electronic properties of these materials.