Investigation on the Structure and Superconducting Properties of Mg1 − x M x B2 (M = deficiency or Ca)
X. P. Zhang,Y. G. Zhao,P. T. Qiao,Z. S. Yin,S. L. Jia,B. S. Cao,M. H. Zhu,Z. H. Han,Y. H. Xiong,P. J. Li,B. L. Gu
DOI: https://doi.org/10.1023/A:1014602321541
2002-01-01
Journal of Superconductivity
Abstract:We report the preparation of Mg 1 − x M x B 2 (M = deficiency or Ca) compounds and their structure and superconducting properties. For Mg 1 − x B 2 , although nearly single-phase samples can be obtained for x = 0, MgB 4 coexists with the MgB 2 phase and some minor impurity phases, and the amount of MgB 4 increases with x for 0 < x ≤ 0.5. The lattice parameters a and c of MgB 2 decreases and increases, respectively, with the increase of x , and T c also decreases. While for Mg 1 − x Ca x B 2 , the superconducting transition temperature remains unchanged for x ≤ 0.3 and loss of superconductivity occurs for x > 0.3. X-ray diffraction patterns for x ≤ 0.3 samples show that MgB 2 phase coexists with CaB 6 , Mg, and MgO. With increasing x , the amount of CaB 6 , Mg, and MgO increases, while the amount of MgB 2 decreases. The lattice parameters of MgB 2 phase do not show any obvious change in contrast to Mg 1 − x B 2 . The results were discussed by considering some possible contributions.