Preparation of Ag-doped Mg1-xAgxB2 superconductors

JianDong Guo,Xiaolin Xu,Yongzhong Wang,Lingying Shi,Dayong Liu

DOI: https://doi.org/10.1016/j.matlet.2004.07.019

IF: 3

2004-01-01

Materials Letters

Abstract:We report the preparation of Ag-doped MgB2 through solid-state reactions. All the obtained Mg1−xAgxB2 bulk samples were examined using XRD, SEM, magnetization and resistance measurements. Both R–T and M–T results indicate that the sample Mg0.9Ag0.1B2 remains superconducting, but with a slightly lower transition temperature and broader transition width than the pure binary MgB2. At higher doping levels of x=0.3, a transition into diamagnetism was observed; however, no zero resistance, as shown by the R–T measurement, occurred in the measured range (min. T=10 K). SEM observation showed a layered grown crystal morphology. It seems to be difficult to index the X-ray diffraction pattern by means of the known pure phases.