Abstract:All-solid-state lithium batteries (ASSLBs) are regarded as the next-generation energy storage devices due to their superior safety and potential high energy density. In ASSLBs, a composite solid electrolyte is the most competitive candidate. The interface between the cathode and composite electrolyte and the interface between ceramic and polymers are important factors affecting the performance of solid-state batteries. The interface between the superionic conductor and polymer electrolyte (polyvinylidene fluoride) was modified by in situ synthesis of a pyrochlore-type La2Sn2O7 (LSO) ceramic layer on the surface of Li6.4La3Zr1.4Ta0.6O12 (LLZTO). The synthesis of LSO consumes La in LLZTO, increases the concentration of lithium ions in LLZTO, and significantly improves the conductivity of the composite electrolyte (). Compared with the pristine sample (3.15 × 10–5 S cm–1), the conductivity of %LSO-CSE was improved by an order of magnitude (as high as 1.30 × 10–4 S cm–1). At the same time, the lithium-ion transference number of %LSO-CSE and %LSO-CSE was 0.42 and 0.44, respectively (%LSO-CSE was 0.36). Meanwhile, the pyrochlore structure of LSO has the characteristics of fast energy storage and conversion, so the full cell LiFePO4||Li showed superior rate capability and cycling stability. As anticipated, the discharge capacities of LiFePO4|%LSO-CSE|Li were 141.4 mA h g–1 (1 C) and 128.1 mA h g–1 (2 C), respectively. However, the discharge capacities of pristine batteries without LLZTO modification were 122.5 mA h g–1 (1 C) and 88.7 mA h g–1 (2 C). After 400 cycles, the discharge capacity of the LiFePO4|%LSO-CSE|Li remained at 110.6 mA h g–1, the Coulomb efficiency was 99.4%, and the capacity retention rate was 72% compared to 75.5 mA h g–1, 98, and 49% for the pristine one, respectively. In addition, the transfer printing (TP) technology was used to improve the interface between the cathode and the solid-state electrolyte, which immensely increased the energy density (without aluminum foil). Compared with the original interface impedance of 379 Ω, the interface impedance was significantly reduced to 213 Ω. This uniquely developed combined with the TP technology can provide an effective approach for the development of all-solid-state batteries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c09692.SEM images and EDS maps of ; particle size distribution of LLZTO; optical photographs of the tensile test of the composite electrolyte membrane; electronic conductivity of ; and galvanostatic cycles of Li|%LSO-CSE|Li (PDF)This article has not yet been cited by other publications.

A novel thin solid electrolyte film and its application in all-solid-state battery at room temperature

The Synthesis and Application of Llzo Ultrathin Electrolyte Film

Compatibility of Li7La3Zr2O12 Solid Electrolyte to All-Solid-State Battery Using Li Metal Anode

Isomeric Li–La–Zr–O Amorphous–Crystalline Composite Thin-Film Electrolytes for All-Solid-State Lithium Batteries

Li/Li7La3Zr2O12/LiFePO4 All-Solid-State Battery with Ultrathin Nanoscale Solid Electrolyte

Highly conductive thin lamellar Li7La3Zr2O12/Li3InCl6 composite inorganic solid electrolyte for high-performance all-solid-state lithium battery

Preparation and electrochemical properties of LLZO co-doping with Al and Ti for all solid-state battery

Thin laminar inorganic solid electrolyte with high ionic conductance towards high-performance all-solid-state lithium battery

Slurry Casted Ultrathin Li3Zr2Si2PO12 Electrolyte Film for Solid‐State Lithium Metal Batteries

Elastic and well-aligned ceramic LLZO nanofiber based electrolytes for solid-state lithium batteries

Fast Charge Transfer between LLZO Solid Electrolyte and LCO Cathode Thin Films with a Modified Interface

Li6.75La3Zr1.75Ta0.25O12@amorphous Li3OCl composite electrolyte for solid state lithium-metal batteries

One-Step Processing of Soft Electrolyte/Metallic Lithium Interface for High-Performance Solid-State Lithium Batteries

In-situ constructed lithium-salt lithiophilic layer inducing bi-functional interphase for stable LLZO/Li interface

Sol–gel Derived Li–La–Zr–O Thin Films As Solid Electrolytes for Lithium-Ion Batteries

Artificially Transformed Ultra-Stable Li6.75La3Zr1.75Ta0.25O12 Incorporated Composite Solid Electrolyte Towards High Voltage Solid Lithium Metal Batteries

A high energy and power all-solid-state lithium battery enabled by modified sulfide electrolyte film

Room-temperature fabrication of garnet-type solid-electrolyte: Optimizing particle size for high ionic conductivity

All-Solid-State Lithium-Ion Batteries with Oxide/Sulfide Composite Electrolytes

A Study on PVDF-PEO-Li7La2.5Ce0.5Zr1.625Bi0.3O12 Solid Electrolyte with High Ionic Conductivity and Its Application in Solid-State Batteries

Interface Improvement of Li 6.4 La 3 Zr 1.6 Ta 0.6 O 12 @La 2 Sn 2 O 7 and Cathode Transfer Printing Technology with Splendid Electrochemical Performance for Solid-State Lithium Batteries