Ultra-high Photoresponsivity in Suspended Metal-Semiconductor-Metal Mesoscopic Multilayer MoS2 Broadband Detector from UV-to-IR with Low Schottky Barrier Contacts

Gustavo A. Saenz,Goran Karapetrov,James Curtis,Anupama B. Kaul

DOI: https://doi.org/10.1038/s41598-018-19367-1

IF: 4.6

2018-01-19

Scientific Reports

Abstract:The design, fabrication, and characterization of ultra-high responsivity photodetectors based on mesoscopic multilayer MoS2 is presented, which is a less explored system compared to direct band gap monolayer MoS2 that has received increasing attention in recent years. The device architecture is comprised of a metal-semiconductor-metal (MSM) photodetector, where Mo was used as the contact metal to suspended MoS2 membranes. The photoresponsivity R$${\boldsymbol{R}}$$ was measured to be ~1.4 × 104 A/W, which is > 104 times higher compared to prior reports, while the detectivity D* was computed to be ~2.3 × 1011 Jones at 300 K at an optical power P of ~14.5 pW and wavelength λ of ~700 nm. In addition, the dominant photocurrent mechanism was determined to be the photoconductive effect (PCE), while a contribution from the photogating effect was also noted from trap-states that yielded a wide spectral photoresponse from UV-to-IR (400 nm to 1100 nm) with an external quantum efficiency (EQE) ~104. From time-resolved photocurrent measurements, a decay time τd ~ 2.5 ms at 300 K was measured from the falling edge of the photogenerated waveform after irradiating the device with a stream of incoming ON/OFF white light pulses.

multidisciplinary sciences