Abstract:This series of studies aims to design acrylate-terminated polyurethanes for use in nylon seamless bonded fabrics. The first part used N,N-dimethylacrylamide (DMAA) and methyl methacrylate (MMA) to replace the chain extender in polyurethane synthesis as end-capping agent to synthesize thermoplastic polyurethane (TPU) adhesive. The molecular weight of the TPU is controlled to further influence the mechanical and processing properties of the polyurethane. Here, polytetramethylene ether glycol (PTMG) and 4,4-methylene diphenyl diisocyanate (MDI) were polymerized, and then a blocking agent was added thereto. The results show that the characteristic peaks of benzene ring and carbamate of TPU adhesive are at 1596 cm−1 and 1413 cm−1, respectively, while the characteristic peaks of DMAA are at 1644 cm−1 and 1642 cm−1 in the FT-IR spectrum. There is an absorption peak –N=C=O– which is not shown near 2268 cm−1, which proves that the structure of TPU contains the molecular structure of capping agent, PTMG and MDI. When the DMAA concentration in the capping agent was increased from 3.0 wt% to 10 wt%, the –C=O (H-bond) area percentage of hydrogen bonds formed at 1711 cm−1 increased from 41.7% to 57.6%, while the –NH (H bond) produced at 3330 cm−1 increased from 70% to 81%. These phenomena suggest that increasing the concentration of DMAA capping agent can effectively promote the formation of complex supramolecular network structures by hydrogen bonding in TPU. The content and concentration of the capping agent affects the molecular weight of the TPU. Chain growth is terminated when molecular weight growth can be effectively controlled and reduced. It was observed in thermal analysis that with increasing DMAA concentration in the molecular structure, the concentration of capping agent in TPU, hydrogen bonding force between hard segments, melting point (Tmh) and melting enthalpy (ΔH) all increased the capping agent. The pyrolysis temperature of TPU is increased by 10–20 °C.

Hot-melt pressure-sensitive adhesive for seamless bonding of nylon fabric part I: effect of a functional monomer

Hot-melt pressure-sensitive adhesive for seamless bonding of nylon fabric Part II: Process parameter optimization for seamless bonding of nylon fabric

UV‐photopolymerized acrylic pressure‐sensitive adhesives with semi‐interpenetration structure: Effect of plasticizer structures on adhesion properties

Influence of Acrylonitrile Content on the Adhesive Properties of Water-Based Acrylic Pressure-Sensitive Adhesives

Synthesis, characterization, and pressure-sensitive properties of butyl acrylate and methyl acrylate copolymers

Studies on the influence of soft-segment structure on the properties of polyurethane adhesive

Adhesive Performance of Acrylic Pressure-Sensitive Adhesives from Different Preparation Processes

Poly(2-ethyl hexyl acrylate-co-methyl allyl polyethylene glycols ether–co-acrylic acid) pressure-sensitive adhesives: synthesis, characterization, investigations of adhesive and thermal properties

Influence of Acrylic Acid on Kinetics of UV-Induced Cotelomerization Process and Properties of Obtained Pressure-Sensitive Adhesives

Synthesis and Characterization of Pressure-Sensitive Adhesives Based on a Naphthyl Curing Agent

Feasibility of Processing Hot-Melt Pressure-Sensitive Adhesive (HMPSA) with Solvent in the Lab

Design of Acrylate-Terminated Polyurethane for Nylon Seamless Bonding Fabric Part I: Design of the End-Capping Thermoplastic Polyurethane Adhesive with Acrylate Copolymer

Synthesis and Properties of Water-Based Acrylic Adhesives with a Variable Ratio of 2-Ethylhexyl Acrylate and n-Butyl Acrylate for Application in Glass Bottle Labels

Study on Preparation and Property of Hot Melt Pressure Sensitive Adhesive Used for Labels

Synthesis and Structure–property Relationships of SIS-g-PB Copolymers and Their Application in Hot-Melt Pressure-Sensitive Adhesives

Rheological Properties of Hot Melt Pressure Sensitive Adhesives (HMPSAs) Based on Styrene–Isoprene Copolymers, Part 3: Rheological Behavior of Different Block Copolymers With High Diblock Content

Preparation of environmentally friendly acrylic pressure-sensitive adhesives by bulk photopolymerization and their performance

Fabrication of acrylic pressure-sensitive adhesives containing maleimide for heat-resistant adhesive applications

Synergistic improvement on both the oil-resistance and heat-resistance performance of a single-component acrylic pressure-sensitive adhesive

Effect of side group and crosslinking on the copolyesters as solvent-free pressure-sensitive adhesives

Preparation and characterization of long carbon chain based polyacrylate latexes and their pressure sensitive adhesive application