Abstract:This study investigates the impact of cryogenic treatment duration on the mechanical properties and microstructural evolution of 6082 aluminum alloy subjected to subsequent artificial aging. Tensile tests were conducted using an electronic universal testing machine, and the microstructure was characterized by employing optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results indicate that both the tensile strength and elongation of the alloy first increase and then decrease with the extension of cryogenic treatment duration. The alloy treated with 12 h of cryogenic treatment followed by artificial aging at 180 °C for 8 h achieved a peak strength of 390 MPa. Meanwhile, the alloy treated with 8 h of cryogenic treatment and the same artificial aging process reached a maximum elongation of 13%. All specimens of 6082 aluminum alloy subjected to cryogenic and aging treatments exhibited ductile fracture under room temperature tensile conditions. The size of dimples at the fracture surface first increased and then decreased with increasing cryogenic treatment duration, indicating a transition from deeper to shallower dimples. The cryogenic treatment did not significantly affect the grain size of the alloy, which remained approximately 230 μm on average. Cryogenic treatment facilitated the precipitation of fine, densely distributed precipitates, enhancing the pinning effect of dislocations and thus improving the tensile strength. Additionally, cryogenic treatment increased the dislocation density and promoted the formation of subgrains, while the grain boundary precipitates transitioned from a continuous to a discontinuous distribution, all of which contribute to the enhancement of the plasticity.

Effects of deep cryogenic treatment on microstructural evolution and alloy phases precipitation of a new low carbon martensitic stainless bearing steel during aging

Effects of traditional heat treatment and a novel deep cryogenic treatment on microstructure and mechanical properties of low-carbon high-alloy martensitic bearing steel

Effect of multiple deep cryo-treating and tempering on microstructure and property evolution of high carbon bearing steel

Effect of deep cryogenic treatment on martensitic lath refinement and nano-twins formation of low carbon bearing steel

Effect of Deep Cryogenic Time on the Microstructure and Mechanical Property of Cr-Mn-Si High-Strength Alloy Steel

Experimental Investigation on the Effect of Deep Cryogenic Treatment on 100Cr6 Bearing Steel

Effect of Deep Cryogenic Time on Martensite Multi-Level Microstructures and Mechanical Properties in AISI M35 High-Speed Steel

Experimental Investigation on the Effect of Deep Cryogenic Treatment on 100 Cr6 Bearing Steel

Effect of deep cryogenic treatment on the microstructure and mechanical properties of Al–Cu–Mg–Ag alloy

Interpretation of microstructure evolution and mechanical properties under aging treatments of a Fe–24Mn-0.6C–2Al-0.6V austenitic steel for cryogenic application

Effects of deep cryogenic treatment on the microstructure evolution, mechanical and thermal fatigue properties of H13 hot work die steel

Effects of deep cryogenic treatment on microstructure, mechanical, and corrosion of ZK60 Mg alloy

Effect of Pulsed Magnetic Field on Retained Austenite of Quenched 8cr4mo4v Steel under Cryogenic Condition

Enhancing Ductility of Martensitic Steels Through Cryogenic Treatment

Effectively improving the hardness-strength-toughness of carburized bearing steel via nanoprecipitates and fine grain structure

Hardness and toughness investigations of deep cryogenic treated cold work die steel

Effect of Deep Cryogenic Aging Treatment on Microstructure and Mechanical Properties of Selective Laser-Melted AlSi10Mg Alloy

The Strengthening Role of Cryogenic Treatment in the Mechanical Properties and Abrasive Wear of Low Alloy Wear-Resistant Steel

Effect of Deep Cryogenic Treatment on the Artificial Aging Behavior of 6082 Aluminum Alloy

Influence of deep cryogenic treatment on internal friction behavior in the process of tempering

Carbides precipitation and kinetics of H13 steel subjected to deep cryogenic treatment