Abstract:Herein, the cryogenically martensitic transformation and its effects on the tempering behaviors of bearing steel was investigated. An in-situ magnetic method was used for obtaining the thermodynamics of the martensitic transformation at sub-zero Celsius temperature from in respects of athermal and isothermal conditions. Microstructure evolution was also characterized systematically to investigate the mechanisms of the martensitic transformation. The results showed that the athermally martensitic transformation of samples experienced three different stages, where the martensite formed slowly at 300–230 K, rapidly at 230–120 K, and slowly again at 120–77 K during the continuous cooling process. With the increase of cooling rate, both the start and finish temperatures of the transformation rise, while the maximum transformed rate decreases. The content of retained austenite transformed isothermally is much smaller as compared to the athermal condition. The amount of isothermally formed martensite does not show linear relationship with the temperature, where an optimal isothermal temperature for GCr15 steel is 193 K in this work. XRD measurement result showed that the content of retained austenite decreased with the decrease of treating temperature in practical DCT, where the content was reduced up to 4.2% after DCT at the lowest temperature combined with tempering. DCT enhanced the precipitation of θ-carbides during tempering and altered the precipitation behavior by advancing the precipitated temperature of θ-carbides from 340 °C to 315 °C. The tempered hardness of samples was improved by DCT, which can be attributed to the enhanced carbides precipitation during tempering and lower content of retained austenite after DCT. The improvement was also affected by tempering and austenitizing temperatures. It was concluded that the performance improvement induced by DCT was most evident if DCT was conducted between higher temperature quenching and lower temperature tempering. DCT also affected the decomposition of retained austenite during tempering by decreasing the activation energy of decomposition by up to 38.13 KJ/mol, which indicated a lower thermal stability of retained austenite after DCT. Microstructure observation indicated that the substructure of the new formed martensite was dominated by ultra-fine twins, which derived from the accommodated strain induced by martensitic transformation during DCT. The transformation strain induced by DCT also causes more dislocations in the microstructure, which provides more nucleation sites for the precipitation of θ-carbides during tempering.

Influence of deep cryogenic treatment on internal friction behavior in the process of tempering

Effect of multiple deep cryo-treating and tempering on microstructure and property evolution of high carbon bearing steel

Effect of deep cryogenic treatment on carbon segregation in Cr8Mo2SiV tool steel during tempering

Carbides precipitation and kinetics of H13 steel subjected to deep cryogenic treatment

Effects of traditional heat treatment and a novel deep cryogenic treatment on microstructure and mechanical properties of low-carbon high-alloy martensitic bearing steel

Cryogenically martensitic transformation and its effects on tempering behaviors of bearing steel

Effects of deep cryogenic treatment on the microstructure evolution, mechanical and thermal fatigue properties of H13 hot work die steel

Effects of deep cryogenic treatment on microstructural evolution and alloy phases precipitation of a new low carbon martensitic stainless bearing steel during aging

Influence of Deep Cryogenic Treatment on Microstructures and Mechanical Properties of an Ultrafine-Grained WC-12Co Cemented Carbide

Effect of deep cryogenic treatment on martensitic lath refinement and nano-twins formation of low carbon bearing steel

Effect of Deep Cryogenic Treatment on the Carbide Precipitation and Tribological Behavior of D2 Steel

Effects of deep cryogenic treatment on the microstructure and mechanical properties of an ultrahigh-strength TRIP-aided bainitic steel

Effects of Deep Cryogenic Treatment on Tribological Properties of the Tool Steel DC53

Influence of shallow and deep cryogenic treatment on the residual state of stress of 4140 steel

Hardness and toughness investigations of deep cryogenic treated cold work die steel

Influence of Deep Cryogenic Treatment and Secondary Tempering on Microstructure and Mechanical Properties of Medium-Carbon Low-Alloy Steels

Effect of deep cryogenic treatment on microstructures and mechanical properties of automotive 6063Al alloy

Enhancing the Wear Resistance of 100Cr6 Bearing Steel Using Cryogenic Treatment

Effect of tempering and deep cryogenic treatment on microstructure and mechanical properties of Cr–Mo–V–Ni steel