Abstract:Abstract The drive to higher efficient gas turbine engines and improved performance is attained by increasing turbine inlet temperature. This lead to the use of advanced material, multi-layered thermal barrier coatings (TBCs) and effective cooling technique in a gas turbine blade system. The main objective is to predict and compare the life between an uncoated blade developed by NASA named C3X and a tri-layered thermal barrier coated C3X blade working under four different high temperature operating conditions. The geometry of the uncoated blade was modelled using Catia software. Three layers of coatings i.e., top coat, bond coat and thermally grown oxide with suitable thickness were generated by the mesh offset technique which was applied to an uncoated blade to model the coated blade. Thereafter steady-state 3D conjugate heat transfer analysis (CFD) with k-ε turbulence model by Ansys Cfx was performed to obtain temperature, pressure and heat transfer coefficient distribution on the surface of the blade. Firstly, this CFD analysis was performed using stainless steel as substrate material, then validated with experimental values and lastly, the same simulation model was applied to Nickel based super-alloy CMSX-4 material. The next step was carrying out transient uncoupled heat transfer, thermal stress, mechanical stress and sequentially coupled thermo-mechanical stress analyses using Abaqus for a flight length of 5000 seconds. At last, the creep-fatigue interaction life of the blade was computed by ductility exhaustion concept with morrow mean stress correction method using Fesafe/Turbolife software. After carrying out above mentioned processes for both uncoated and coated blade, an effective comparison was made. A significant decrease in Temperature (up to 127 K) and Thermo-Mechanical Stress (up to 263 MPa) and a significant increase in Fatigue-Creep Life (up to 16.5 times) was observed when TBCs were applied. The result shows that the thermal load was more severe than the mechanical load. The maximum thermo-mechanical stress was found at the trailing edge and fixed portion of the blade.

Effect of Aluminized Coating on Combined Low and High Cycle Fatigue Life of Turbine Blade at Elevated Temperature

Microstructure Degradation of Service-Exposed Turbine Blades Made of Directionally Solidified DZ125 Superalloy

Service Damage Mechanism and Interface Cracking Behavior of Ni-based Superalloy Turbine Blades with Aluminized Coating

Accelerated damage mechanisms of aluminized superalloy turbine blades regarding combined high-and-low cycle fatigue

Probing the failure mechanisms and microstructure evolution of a high-pressure turbine blade coated with AlSiY

Thermomechanical Fatigue Experiment and Failure Analysis on a Nickel-Based Superalloy Turbine Blade

Microstructure degradation and residual low cycle fatigue life of a serviced turbine blade

The Analysis on the Low Cycle Fatigue Behavior of A Directionally Solidified Superalloy with Recrystallized Surface Layers

Analysis of Fatigue Cracking for Turbine Blade

Competitive Cracking Behavior and Microscopic Mechanism of Ni-based Superalloy Blade Respecting Accelerated CCF Failure

Cr/CrN coating effect on the fatigue crack nucleation period of Ti-6Al-4V alloy

Combined tensile and bending fatigue behavior and failure mechanism of a blade-like specimen at elevated temperature

Coating-assisted deterioration mechanism of creep resistance at a nickel-based single-crystal superalloy

Life Prediction of Thermal Barrier Coated C3X Gas Turbine Blade of CMSX-4 Material

Effect of Surface Coating on Low Cycle Fatigue Behavior of Nickel- Based Directionally Solidified Superalloy

Research on low‐cycle fatigue behavior of Ni‐based single crystal superalloy with shaped film cooling holes at high temperature

A novel fatigue life model for MCrAlY coated superalloys considering interfacial microstructure evolution

Role of the pre-existed cracks in the high-cycle fatigue properties of the Al-Si coated press hardened steel

Stress-sensitive fatigue crack initiation mechanisms of coated titanium alloy

Low-cycle fatigue of MCrAlY-coated superalloys: a fracture mechanics-based analysis

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method