Abstract:Several investigations on physical vapor deposition (PVD) coated steel substrates under cyclic bending load have reported an increase in fatigue strength of the coated compound. The compressive residual stress state of the coating can delay the initiation and propagation of surface or subsurface fatigue cracks. There are also investigations reporting no significant effect or a negative effect of PVD coatings on fatigue behavior of steels. The argument here is that the coating cracks during deformation and may lead to an earlier crack initiation in the substrate. Therefore, the effect of PVD coatings on fatigue behavior needs to be studied independently for different substrate materials. Here, the investigations on fatigue behavior of PVD coated tool steels are rather limited. Moreover, the fatigue damage mechanisms have been analyzed ex situ after the sample failure mostly for low stress amplitudes. The presented work is aimed at investigating the effect of CrAlN coating on the fatigue behavior of HS6–5-2C tool steel along with the analysis of fatigue cracks initiation and propagation in coated compound. For this purpose, the fatigue behavior of uncoated and coated tool steel was studied at high as well low bending stress amplitudes. Scanning electron microscopy (SEM) was used to analyze the fractured samples. Moreover, the fatigue damage mechanism in coated compound was studied in situ by carrying out a cyclic bending test inside large chamber SEM. It was shown that the fatigue damage in PVD coated high speed tool steel compounds under cyclic bending load is largely initiated in the substrate at low stress amplitudes. Here, the large carbide particles, carbide clusters or nonmetallic inclusions at the substrate surface or subsurface act as fatigue crack initiation sites. Depending on bending stress amplitude and residual stress state of the PVD coating, the coating may resist the propagation of fatigue cracks in certain cases to positively influence the fatigue behavior of tool steel substrate. The investigation contributes to fundamental understanding of fatigue damage in PVD coated tool steel compounds.

Role of the pre-existed cracks in the high-cycle fatigue properties of the Al-Si coated press hardened steel

Stress-sensitive fatigue crack initiation mechanisms of coated titanium alloy

Crack Configuration Feature and Fracture Surface Difference for High Pressure Die Casting Hypereutectic Al-Si Alloys in High Cycle Fatigue

Crack Initiation Mechanism in a High-Strength Ti-5Al-7.5V Alloy Subjected to High Cycle Fatigue Loading

Fretting Fatigue Behavior and Damage Mechanism of Cast Al-Si-Cu-T6 Alloy Under Two Surface Roughness conditions

High-cycle fatigue failure analysis of cast Al-Si alloy engine cylinder head

Fatigue Crack-Initiation Mechanisms of a Dual-Phase Titanium Alloy Exhibiting High Tensile and High-Cycle Fatigue Properties

Cyclic Deformation and Microcrack Initiation During Stress Controlled High Cycle Fatigue of a Titanium Alloy

Transformation of carbides and mechanisms for cracking in Co-based alloy surfacing layer during thermal fatigue

A case study on fatigue damage in PVD coated tool steel under cyclic bending load

Experimental Characterization of Competition of Surface and Internal Damage in Very High Cycle Fatigue Regime

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Effect of surface coating on fatigue life and fatigue crack growth behavior of AISI D2 tool steel

Cr/CrN coating effect on the fatigue crack nucleation period of Ti-6Al-4V alloy

A fatigue life prediction approach to interior cracking induced high cycle and very high cycle fatigue for surface‐carburized steels

Studies on Fatigue Properties of Steel with Co-Based Alloy Hardfacing Coating

Quantitative Assessment of Microstructural Damage for Interior Crack Initiation and High Cycle Fatigue Life Modeling

Preparation and deformation behaviour of multi-structural aluminium-coated steels

Effect of Grit Blasting and Subsequent Cold Spraying on Low-Cycle Fatigue Crack Growth of Q355B Steel

An In Situ Study of Short Crack Initiation and Propagation During Fatigue Testing of a Hot Isostatically Pressed Al-7%Si-0.5%Mg (A357-T6) Alloy Specimen

Considerations on the Failure Mechanisms at Fatigue Loading of 1018 Steel Samples Coated with Wip-C1 by Cold Spray