Abstract:In this study, red mud-based CoFe2O4 (CoFe2O4/RM) was firstly prepared via a sol–gel method, and then activated through ball milling to obtain the catalyst of Ball-milled CoFe2O4/RM (BM-CoFe2O4/RM). The BM-CoFe2O4/RM catalyst was applied as a high-efficiency activator of peroxymonosulfate (PMS) for the degradation of lomefloxacin hydrochloride (LOM-HCl). The LOM-HCl (100 mg/L) could be removed 86.36 % after 12 min treatment under the optimal reaction parameters (BM-CoFe2O4/RM dosage of 1.33 g/L, PMS concentration of 5 mmol/L and nature pH 6.59 ± 0.1). The comparative experiments revealed that the apparent rate constant of LOM-HCl degradation of BM-CoFe2O4/RM (0.1091 min−1) was approximately 1.6 times that of CoFe2O4/RM (0.0701 min−1). A series of characterizations demonstrated that the physicochemical properties of CoFe2O4/RM, including defective structures, crystallinity of high active components, exposures of Co (II) and Fe (II) and electrical conductivity, could be improved via ball milling, causing the increase of the catalytic activity of CoFe2O4/RM. Combined with the results of Electron spin resonance (ESR), X-ray photoelectron spectrometer (XPS) and quenching experiments, the possible catalytic mechanism of PMS activated by BM-CoFe2O4/RM for LOM-HCl degradation was proposed. Combined with the density functional theory (DFT) calculation and liquid chromatography-mass spectrometer (LC-MS), the possible vulnerable sites and possible degradation pathways of LOM-HCl were obtained. The recycling experiments and XPS demonstrated that BM-CoFe2O4/RM had good stability, and the catalytic activity of the BM-CoFe2O4/RM after use could be regenerated by thermal treatment. The biological toxic experiment suggested that the toxicity of LOM-HCl solution treated by the BM-CoFe2O4/RM + PMS system was effectively reduced. The work not only provides a simple and high-efficiency method for improving the catalytic activity of CoFe2O4/RM, but also opens novel insights into the Ball-milled CoFe2O4/RM as an effective PMS activator for antibiotic wastewater treatment.

Synthesis of magnetic NiFe2O4/CuS activator for degradation of lomefloxacin via the activation of peroxymonosulfate under simulated sunlight illumination

Red mud-based CoFe2O4 activated by ball milling as effective peroxymonosulfate activator for the degradation of lomefloxacin hydrochloride: Preparation & activation, application and degradation mechanism

Acceleration of levofloxacin degradation by combination of multiple free radicals via MoS2 anchored in manganese ferrite doped perovskite activated PMS under visible light

MnFe 2 O 4 nanoparticles coated on one-dimensional carbon nanowires derived from Nitrilotriacetic acid as efficient catalysts to activate peroxymonosulfate for moxifloxacin degradation

Flower-like bentonite-based Co3O4 with oxygen vacancies-rich as highly efficient peroxymonosulfate activator for lomefloxacin hydrochloride degradation

Enhanced activation of peroxymonosulfate for ofloxacin rapid degradation and inhibition of metal leaching on LaNi0.6Co0.4O3 stably anchored at ZnO

Enhanced activation of peroxymonosulfate by a floating FeMo3Ox/C3N4 photocatalyst under visible-light assistance for oxytetracycline degradation: Performance, mechanisms and comparison with H2O2 activation

Peroxymonosulfate activation by Co-doped magnetic Mn3O4 for degradation of oxytetracycline in water

Efficient light-driven peroxymonosulfate activation by CoS /TiO nanorod for rapid degradation of levofloxacin: Performance and continuous degradation process

Enhanced activation of persulfate by magnetic NiFe2O4@CuO coupled with ultrasonic for degradation of oxytetracycline: Activation mechanism and degradation pathway

Enhanced activation of persulfate by magnetic NiFe 2 O 4 @CuO coupled with ultrasonic for degradation of oxytetracycline: Activation mechanism and degradation pathway

Enhanced degradation of tetracycline hydrochloride by activated peroxymonosulfate through Ni-doped LaFeO 3

Efficient Degradation of Ofloxacin by Magnetic CuFe2O4 Coupled PMS System: Optimization, Degradation Pathways and Toxicity Evaluation

Activation of peroxymonosulfate by a stable Co-Mg-Al LDO heterogeneous catalyst for the efficient degradation of ofloxacin

Magnetic CuFe2O4 Nanoparticles Immobilized on Mesoporous Alumina As Highly Efficient Peroxymonosulfate Activator for Enhanced Degradation of Tetracycline Hydrochloride

Construction of Lamellar CoFe-LDHs@MoS2 to Promote Permonosulfate Properties Leading to Effective Photocatalytic Degradation of Norfloxacin

[Degradation of Ciprofloxacin by CuNiFe LDHs/BiO2- x Heterojunction-activated Peroxymonosulfate Under Visible Light Irradiation]

Enhanced activation performance of peroxymonosulfate by NiCo2O4/SnO2 composite for metronidazole degradation under visible light

Inverse opal manganese-doped tungsten trioxide as a high-performance Fenton-like photocatalyst for levofloxacin degradation

Phosphorus-modified copper ferrite (P-CuFe2O4) nanoparticles for photocatalytic ozonation of lomefloxacin

Bio-synthesis of Co-doped FeMnOx and its efficient activation of peroxymonosulfate for the degradation of moxifloxacin