Abstract:In this study, red mud-based CoFe2O4 (CoFe2O4/RM) was firstly prepared via a sol–gel method, and then activated through ball milling to obtain the catalyst of Ball-milled CoFe2O4/RM (BM-CoFe2O4/RM). The BM-CoFe2O4/RM catalyst was applied as a high-efficiency activator of peroxymonosulfate (PMS) for the degradation of lomefloxacin hydrochloride (LOM-HCl). The LOM-HCl (100 mg/L) could be removed 86.36 % after 12 min treatment under the optimal reaction parameters (BM-CoFe2O4/RM dosage of 1.33 g/L, PMS concentration of 5 mmol/L and nature pH 6.59 ± 0.1). The comparative experiments revealed that the apparent rate constant of LOM-HCl degradation of BM-CoFe2O4/RM (0.1091 min−1) was approximately 1.6 times that of CoFe2O4/RM (0.0701 min−1). A series of characterizations demonstrated that the physicochemical properties of CoFe2O4/RM, including defective structures, crystallinity of high active components, exposures of Co (II) and Fe (II) and electrical conductivity, could be improved via ball milling, causing the increase of the catalytic activity of CoFe2O4/RM. Combined with the results of Electron spin resonance (ESR), X-ray photoelectron spectrometer (XPS) and quenching experiments, the possible catalytic mechanism of PMS activated by BM-CoFe2O4/RM for LOM-HCl degradation was proposed. Combined with the density functional theory (DFT) calculation and liquid chromatography-mass spectrometer (LC-MS), the possible vulnerable sites and possible degradation pathways of LOM-HCl were obtained. The recycling experiments and XPS demonstrated that BM-CoFe2O4/RM had good stability, and the catalytic activity of the BM-CoFe2O4/RM after use could be regenerated by thermal treatment. The biological toxic experiment suggested that the toxicity of LOM-HCl solution treated by the BM-CoFe2O4/RM + PMS system was effectively reduced. The work not only provides a simple and high-efficiency method for improving the catalytic activity of CoFe2O4/RM, but also opens novel insights into the Ball-milled CoFe2O4/RM as an effective PMS activator for antibiotic wastewater treatment.

Flower-like bentonite-based Co3O4 with oxygen vacancies-rich as highly efficient peroxymonosulfate activator for lomefloxacin hydrochloride degradation

Red mud-based CoFe2O4 activated by ball milling as effective peroxymonosulfate activator for the degradation of lomefloxacin hydrochloride: Preparation & activation, application and degradation mechanism

Activation of peroxymonosulfate by a stable Co-Mg-Al LDO heterogeneous catalyst for the efficient degradation of ofloxacin

Synthesis of magnetic NiFe2O4/CuS activator for degradation of lomefloxacin via the activation of peroxymonosulfate under simulated sunlight illumination

CuFe2O4 supported on montmorillonite to activate peroxymonosulfate for efficient ofloxacin degradation

Walnut Shell Loaded with Cobalt Ferrite as Efficient Peroxymonosulfate Activator to Degrade Ofloxacin

Co(CO3)0.5(OH)•0.11H2O as superior peroxymonosulfate activator for ciprofloxacin degradation via co-acting mechanism of low & high-valent cobalt and oxygen vacancy

Activation of peroxymonosulfate by LaCO3OH coupled with N, S co-doped graphene for levofloxacin degradation

Insight into catalytic activation of bisulfite for lomefloxacin degradation by simple composite of calcinated red mud

Enhanced activation of peroxymonosulfate for ofloxacin rapid degradation and inhibition of metal leaching on LaNi0.6Co0.4O3 stably anchored at ZnO

Removal of Levofloxacin by Activation of Peroxomonosulfate Using T-POMs@ZIF-67

Acceleration of levofloxacin degradation by combination of multiple free radicals via MoS2 anchored in manganese ferrite doped perovskite activated PMS under visible light

ZIF-67-derived carbon@Co3S4/CoSO4/MnO polyhedron to activate peroxymonosulfate for degrading levofloxacin: Synergistic effect and mechanism

Bio-synthesis of Co-doped FeMnOx and its efficient activation of peroxymonosulfate for the degradation of moxifloxacin

Phosphorus-modified copper ferrite (P-CuFe2O4) nanoparticles for photocatalytic ozonation of lomefloxacin

Peroxymonosulfate activation by Co-doped magnetic Mn3O4 for degradation of oxytetracycline in water

Oxygen and nitrogen co-doped mesoporous carbon derived from COFs for efficient degradation of levofloxacin via peroxymonosulfate activation

Sulfur-doped mesoporous ferric oxide used for effectively activating H2O2 to degrade moxifloxacin

MOF-derived FeCo carbon nanomaterials with abundant oxygen vacancies as highly efficient peroxymonosulfate catalyst for ciprofloxacin degradation

Covalent organic frameworks derived carbon supported cobalt ultra-small particles: C O and Co-N x complex sites activated peroxymonosulfate synergistically for efficient degradation of levofloxacin

Efficient heterogeneous activation of peroxymonosulfate by manganese-doped LaCoO 3 perovskites for metronidazole degradation: A mechanistic study and reaction pathways