Primary creep X80 pipeline steel at room temperature using molecular dynamics simulation

Peng Wang,Wenqian Hao,Jiamiao Xie,Jian Ding,Fenghui Wang,Chunyong Huo

DOI: https://doi.org/10.1007/s00339-022-05339-w

2022-02-15

Applied Physics A

Abstract:Gas transformation field recognized that X80 pipeline steel would fail in operation occasionally some days after pressure stabilized, commonly referred to as a time-delayed failure. Standard creep test usually presents an average and macrostructure results, but understand creep behavior at crystal size level is still interesting. This paper presents the analysis results of the primary creep behavior at dislocation evolution under some stress levels using molecular dynamics (MD) simulation. The polycrystalline model in the base metal region under the different retaining stresses (305 MPa, 427 MPa and 549 MPa), the different stress rates (25 MPa/ps, 50 MPa/ps and 100 MPa/ps) and the cyclic loading history are applied and analyzed using MD simulation. The effects of retaining stress, stress rate and cyclic loading history on the creep deformation of the X80 pipeline steel are investigated. The primary creep increases with the increment of retain stress, but little moving dislocation is produced under 50% minimum yield stress (305 MPa), the primary creep at reloaded retain stress is lower than that of the first load, which is thought as the decrease of moving dislocations. The high stress-loaded rate also results in a decrease primary creep. In addition, the defects and dislocation density under different conditions are analyzed and the room temperature creep mechanism of the model is discussed. The results obtained from this study will provide a reference to the research of room temperature creep of X80 pipeline steel.