Effect of Sodium Hydroxide Additive on Mechanical Properties and Durability of Self-Compacting Concrete with Sulfate Aggregates in Chloride Environment

Alireza Hajiani Boushehrian

DOI: https://doi.org/10.1007/s40996-022-00820-1

2022-02-24

Abstract:Depending on the characteristics of the selected mine, concrete aggregates can include clean or contaminated sand and gravel. This study investigated the effect of contaminated aggregates prone to expansion reaction and simulated destructive environment on the compressive, flexural, and tensile strengths, water absorption, permeability, chloride ion, and freezing–thawing of self-compacting concrete (SCC) samples. The samples were studied in terms of strength and durability at different ages. The contaminated materials were extracted from gravel and sand mines with an impurity exceeding the permissible 0.4% set by the Iranian National Building Code (Part 8). To evaluate the samples' durability, workability, and mechanical properties, slump, U-Box, L-Box, and V funnel tests were performed on the SCC. The SCC samples with clean aggregate were used once with the admixture of sodium hydroxide and once without the admixture as a control sample. Then, SCC samples with sulfate aggregate were made with sodium hydroxide additive with different percentage (2%, 2.5%, and 3%) of water weight to study the inhibition of destructive effects in the chloride environment. Finally, the samples were compared in terms of durability performance and mechanical properties using the obtained results. Based on the results, it can be concluded that sulfate aggregate in a chloride environment reduces the mechanical strength and durability of SCC. Besides, adding sodium hydroxide to SCC samples containing sulfate aggregate increases their durability and mechanical strength while reducing the workability of concrete.