Abstract:Influence of Bacillus Subtilis ( B. Subtilis ) bacteria on the strength characteristics of 100% recycled concrete aggregate (RCA), incorporating silica fume (SF) as a substitution of cement, has been investigated in this study. Two groups of mixes (A for w/c=0.3 and B for w/c=0.35) were prepared using two different cement contents in each (400 and 450 kg/m 3 ). The cement was partially substituted by weight with 5%, 7.5%, and 10% SF, with a constant concentration of bacterial culture (10 5 cfu/ml). All specimens were tested after a curing period of 7, 28, and 90days. The best results were observed by replacing cement with 7.5% SF via all mixes, with the best mix being A/2. At 90 days, the compressive strength (CS) of concrete in mix A/2 increased from 29.62 to 33.64 MPa for 5% SF, from 29.62 to 37.3 MPa for 7.5% SF and from 29.62 to 34.04 MPa for 10% SF with the addition of B. Subtilis bacteria. Similarly, for splitting tensile strength (STS) at 90days, the strength increased from 2.73 to 3.24 MPa for 5% SF, from 2.73 to 3.35 MPa for 7.5% SF, from 2.73 to 3.26 MPa for 10% SF. Calcite precipitation upon addition of B. Subtilis bacteria is considered the reason for the improved CS and STS of concrete, and SEM and EDS analysis confirmed this. Thereby, the formation of new C-S-H products and CaCO 3 crystals in voids made the concrete denser. Incorporation of B. subtilis led to a 12 ± 1.5% increase in CaCO 3 formation in concrete's mortar after 7days of curing compared to specimens without bacteria. Moreover, the effect of atomic Ca/Si and Al + Fe)/Ca ratios was studied, and the results showed that the highest CS and STS were associated with the values Ca/Si = 0.17 and Al + Fe)/C = 2.95. Meanwhile, it is noteworthy that according to the Indian specifications (IS-10262–2009), based on the strength of the concrete, the findings of this work fulfill the requirements of lean, ordinary grade, and standard grade concrete. An economic study of all mixes has also been carried out. Additionally, using response surface methodology, a regression equation was developed to accurately predict the CS and STS and validate the data in this experimental work with a minimum range of error.

Investigating the combined effect of aggregate size and sulphate attack on producing sustainable recycled aggregate concrete

Development of Sustainable Self-Compacting Concrete Using Recycled Concrete Aggregate and Fly Ash, Slag, Silica Fume

Mechanical and Durability Properties of Sustainable Self-Compacting Concrete with Recycled Concrete Aggregate and Fly Ash, Slag and Silica Fume

Investigating the Effects of Recycled Aggregate and Mineral Admixtures on the Mechanical Properties and Performance of Concrete

Experimental Study on Self Compacting Fibrous Concrete Comprising Magnesium Sulphate Solution Treated Recycled Aggregates

Sulfate Resistance and Alkali-Silica Reaction of Recycled Aggregate Concrete

Influence of silica fume and Bacillus subtilis combination on concrete made with recycled concrete aggregate: Experimental investigation, economic analysis, and machine learning modeling

Effect of Acid Treated Recycled Aggregate On Properties of Concrete

Deicer Salt-Scaling Resistance of Concrete Using Recycled Concrete Aggregates Pretreated by Silica Fume Slurry

Experimental Investigation of Self-Compacting Concrete with Recycled Concrete Aggregate

Effect of sulfate attack on multiple interfacial transition zones of high-belite sulfoaluminate cement recycled concrete

Strength, shrinkage and creep and durability aspects of concrete including CO2 treated recycled fine aggregate

Sulfate Ion Diffusion Test of Recycled Aggregate Concrete with Different Replacement Ratio

Influence of Surface Treatment of Recycled Aggregates on Mechanical Properties and Bond Strength of Self-Compacting Concrete

Mitigating sulfate ions migration in concrete: A targeted approach to address recycled concrete Aggregate's impact

Durability performance of alkali-activated concrete with pre-treated coarse recycled aggregates for pavements

Sulfate resistance of ultra-high performance concrete with recycled fine aggregate

The Impact of castoff aggregate on the fresh and mechanical behaviour of high-range water reducer administered self-compacting concrete

Effect of Sodium Hydroxide Additive on Mechanical Properties and Durability of Self-Compacting Concrete with Sulfate Aggregates in Chloride Environment

The Effect of Fine and Coarse Recycled Aggregates on Fresh and Mechanical Properties of Self-Compacting Concrete

Analyzing The Performance of Environmental Friendly Concrete That Contains Acid-Treated (H2so4, H3po4) Recycled Aggregate