Abstract:The microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x = 0, 5, 10, 15) alloys have been studied. XRD and SEM analyses show that all alloys consist of a BCC main phase and a small fraction of C14 Laves secondary phase, in which the latter precipitates along the grain boundary of the former becoming network structure. With increasing Ti content in the alloy, the lattice parameter and cell volume of the BCC main phase of the alloy increase. The chemical composition of each phase is analysed by EDS, from which the lattice parameters of BCC phase have a good linear relationship with their average atomic radii. All bulk alloys have good activation behaviors and hydriding kinetics. With the increase of Ti content, the incubation time for activation decreases first and then increases under an initial hydrogen pressure of 4 MPa at 298 K. The incubation time of Ti15V75Fe6Zr4 alloy is only 12 s. It is one of the shortest incubation time in V-based solid solution alloys as far as we know, which may be related to the existence of C14 Laves phase. All the alloys have relatively high hydrogen absorption capacities of above 3 wt%, which increase first and then decrease as the Ti content increases, achieving the maximum capacity of 3.61 wt% at x = 10 at 298 K. With increasing x, the equilibrium plateau pressure of dehydrogenation of the samples at 353 K decreases owing to the expansion of unit cell of main phase, which is far below 0.1 MPa for x = 10 and 15. The maximum desorption capacity of 1.94 wt% (desorbed to 0.001 MPa) is obtained at x = 5, compared to that of 1.6 wt% (desorbed to 0.1 MPa) achieved at x = 0.

Ti-V-C-Based Alloy with a FCC Lattice Structure for Hydrogen Storage

Development of Ti–Zr–Mn–Cr-(V–Fe) Based Alloys for Hydrogen Feeding System in Hydrogen Metallurgy Application

Experimental and Theoretical Investigation on the Enhanced Hydrogen Storage Performance of Ti–Cr–Mn–Fe-Based Alloys Modified by Nb Substitution

Binding Energy Crossover Mechanism Enables Low-Temperature Hydrogen Storage Performance of Dual-Phase TiZrCrMnNi(VFe) High-Entropy Alloy

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Hydrogen storage properties of V+TiFe0.85Mn0.15 multi-phase alloys

Microstructure and Electrochemical Properties of V2.1TiNi0.4Zr0.06Cux (X=0-0.12) Hydrogen Storage Alloys

Hydrogen storage properties of TiMn2-based alloys

Microstructure and hydrogen storage properties of Ti10V84-xFe6Zrx (x = 1-8) alloys

V 2.1 TiNi 0.4 Zr 0.06 Cu 0.03 M 0.10 (M=Cr, Co, Fe, Nb, Ta)储氢合金的微结构及电化学性能

Structural and Electrochemical Characteristics of V2.1TiNi0.5Hf0.05M0.152 (M = Co, Cr) Hydrogen Storage Electrode Alloys

Hydrogen storage in Ti–V-based body-centered-cubic phase alloys

Microstructures and hydrogen storage characteristics of (Ti0.1V0.9)(100-x)Fe-x (x=0 similar to 6) alloys

TiCr<sub>1.2</sub>(V–Fe)<sub>0.6</sub>—a novel hydrogen storage alloy with high capacity

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

Study on hydrogen storage properties of Ti–V–Fe–Mn alloys by modifying Ti/V ratio

Body-Centered-Cubic Phase Hydrogen Storage Alloy With Improved Capacity And Fast Activation

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Phase structures and electrochemical behaviors of V2.1TiNi 0.5Hf0.05Crx (x=0-0.152) hydrogen storage alloys