Determination of the Intermetallic α-Phase Crystal Structure in Aluminum Alloys Solidified at Rapid Cooling Rates

Joseph Jankowski,Michael Kaufman,Amy Clarke,Krish Krishnamurthy,Paul Wilson

DOI: https://doi.org/10.1007/978-3-030-05864-7_17

2019-01-01

Abstract:Al-Fe-V-Si and Al-Fe-Cr-Si quaternary alloys were produced by arc Melting and chill Casting, and the crystal structures of the \documentclass[12pt]{minimal}\usepackage{amsmath}\usepackage{wasysym}\usepackage{amsfonts}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{mathrsfs}\usepackage{upgreek}\setlength{\oddsidemargin}{-69pt}\begin{document}$$ \upalpha $$\end{document}-phase Intermetallics (Pm-3 or Im-3, a = 1.25–1.27 nm) that formed are compared with those in the well-characterized Al-Mn-Si and Al-Fe-Mn-Si systems produced by arc Melting. The crystal structures were refined using synchrotron x-ray Powder diffraction, and compositions were determined using electron probe microanalysis (EPMA). It was shown that the Al-Fe-Cr-Si, Al-Fe-V-Si, and Al-Fe-Mn-Si systems appear to have the same \documentclass[12pt]{minimal}\usepackage{amsmath}\usepackage{wasysym}\usepackage{amsfonts}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{mathrsfs}\usepackage{upgreek}\setlength{\oddsidemargin}{-69pt}\begin{document}$$ \upalpha $$\end{document}-phase structures after heat treatment at 500 °C. Additionally, a new \documentclass[12pt]{minimal}\usepackage{amsmath}\usepackage{wasysym}\usepackage{amsfonts}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{mathrsfs}\usepackage{upgreek}\setlength{\oddsidemargin}{-69pt}\begin{document}$$ \upalpha $$\end{document}-phase with low Si content was observed in the Al-Fe-V-Si alloys in the as-cast condition.