Abstract:Flower-like titania nanocrystals were synthesized by hydrolysis of titanium (IV) chloride at a low temperature of 70 degrees C in 4-6 h, employing nanocrystal cellulose (NCC) as a morphology controlling agent. The obtained nanocrystals were characterized by transmission electron microscope (TEM), high-resolution transmission electron microscope (HRTEM), X-ray diffraction (XRD) and FTIR. TEM and HRTEM investigations reveal that the morphologies of the nancrystals are flower-like, and each flower is composed of several nanoneedles with a diameter of 15-20 nm and a length of 100-200 nm. The XRD results show that the crystalline phase of the nanocrystals have a strong dependence on the mole ratio of TiCl4 to H2O and the reaction time. FTIR result shows that a chemical bond is formed between NCC and TiO2. A possible growth mechanism is proposed based on the characteristic results. The NCC whose surface is full of hydrophilic groups can establish hydrogen bonding with TiO2 to promote the nucleation and crystal growth of TiO2 at low temperature. Moreover, the selective adsorption of NCC molecules on the crystal face of TiO2 varies the growth rate of different crystal planes, and the anisotropic crystal growth leads to the formation of nanoneedles. Then these nanoneedles aggregate together to assemble into a flower-like secondary structure. TiO2 prepared at low temperature exhibites high activity in the photocatalytic degradation of methyl orange in aqueous solution under metal halide lamp.

Preparation of flower-like titania particles from lithium titanate hydrate via acid treatment and hydrothermal crystallization

Titania Polyhedra Via Sodium Fluorotitanate Intermediates

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Nanocrystalline Titania Made From Interactions Of Ti With Hydrogen Peroxide Solutions Containing Tantalum Chloride

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Alkaline hydrothermal synthesis of homogeneous titania microspheres with urchin-like nanoarchitectures for dye effluent treatments.

Preparation of nanosized titania by hydrolysis of alkoxide titanium in micelles

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Preparation of Hydrated TiO2 Particles by Hydrothermal Hydrolysis of Mg/Al-Bearing TiOSO4 Solution

PREPARATION OF ROD-LIKE RUTILE TiO2 BY SOL-HYDROTHERMAL METHOD

Preparation of spherical TiO2 from TiOSO4 by hydrolysis

Morphology Control of Tio2 Through Hydrothermal Synthesis Method Using Protonic Tetratitanate

Preparation of Nanosized Titania Powder Via the Controlled Hydrolysis of Titanium Alkoxide

Effect of Peptisation on Nanosized TiO2 Particles Prepared by Hydrolysis from Metatitanic Acid

Synthesis and Characterization of Fibrous SrTiO3 Particles

The synthesis of hydrophobic nano-TiO2 powder and its photocatalytic property

Morphology and Photocatalytic Activities of Ultrafine TiO2 Particles Synthesized in High Temperature Aerosol Reactor

Preparation of Square and Labyrinth-Like TiO 2 Particles for Photo-Degradation of Organic Pollutants

Facile Preparation of Ti3+ Self-Doped TiO2 Microspheres with Lichi-Like Surface Through Selective Etching

Preparation and Characterization of Flower-Like Tio2 Induced by Rod-Like Nanocrystalline Cellulose