Direct fabrication of anatase TiO 2 hollow microspheres for applications in photocatalytic hydrogen evolution and lithium storage

Shuai Shi,Yang Chen,Jordan Lee,Zhiyu Jiang,Xiaoli Cui

DOI: https://doi.org/10.1007/s10008-017-3796-8

IF: 2.747

2017-01-01

Journal of Solid State Electrochemistry

Abstract:Hollow titanium dioxide (TiO 2 ) microspheres were synthesized in one step by employing tetrabutyl orthotitanate (TBOT) as a precursor through a facile solvothermal method in the presence of NH 4 HCO 3 . XRD analysis indicated that anatase TiO 2 can be obtained directly without further annealing. TiO 2 hollow microspheres with diameters in the range of 1.0–4.0 μm were confirmed through SEM and TEM measurements. The specific surface area was measured to be 180 m 2 g −1 according to the nitrogen adsorption–desorption isotherms. Superior photocatalytic performance and good lithium storage properties were achieved for resultant TiO 2 samples. The H 2 evolution rate of the optimal sample is about 0.66 mmol h −1 after loaded with 1 wt.% Pt (20 mg samples). The reversible capacity remained 143 mAh g −1 at a specific current of 300 mA g −1 after 100 charge–discharge cycles. This work provides a facile strategy for the preparation of hollow titanium dioxide microspheres and demonstrates their promising photocatalytic H 2 evolution and the lithium storage properties. Graphical abstract Hollow titanium dioxide spheres are directly synthesized via a facile template-free solvothermal method with the presence of NH 4 HCO 3 based on inside-out Ostwald ripening (see picture), and demonstrated both as a photocatalyst for water splitting and a promising anode material for lithium-ion batteries. Superior photocatalytic performance and excellent lithium storage properties are achieved for resultant TiO 2 hollow microspheres.