Abstract:Due to high specific strength and strong toughness, aramid fibre–reinforced plastics have been widely used in the aircraft, military, and automobile industries. However, in the hole-making process, these excellent properties make aramid fibre–reinforced plastics difficult to machine and prone to severe entrance and exit damages. In this article, the cutting mechanisms of three typical tools (twist drill, burr tool, and brad drill) are thoroughly investigated during dry drilling of aramid fibre–reinforced plastic. On this basis, systematic experiments are conducted to evaluate the cutting performance and hole quality. At the hole entrance, the cutting edges of the twist drill peel and tear the uncut material, which results in severe fuzzing damage. Due to the radial rake angles of the burr tool and brad drill, the radial component of the cutting force can pre-tension aramid fibres prior to being cut, which effectively reduces the fuzzing defect. At the hole exit, the extrusion action of the chisel edge and the severe chip adherence are the main causes of exit damage for the twist drill and burr tool, respectively. Due to the decrease in the thrust force and improvement in the shearing action, the best hole quality is achieved by the brad drill. To further improve the hole quality, an auxiliary approach using collars is introduced to effectively restrain the damage by enhancing interfacial bonding strength. This article provides comprehensive and available information on tool performance for drilling aramid fibre–reinforced plastics, which can help guide process optimizations to achieve the desired hole quality.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: under dry - drilling conditions, how to improve the drilling quality of aramid fiber - reinforced plastics (AFRP) and reduce the entrance and exit damages generated during the drilling process. Specifically, by studying the cutting mechanisms of three typical drill bits (twist drill, countersink drill, spot - facing drill) when drilling AFRP, the author aims to reveal the influence of different tools on the hole quality, thereby providing guidance for optimizing the processing technology. ### Problem Background Aramid fiber - reinforced plastics (AFRP) are widely used in the aviation, military, and automotive industries due to their high strength and good toughness. However, these excellent properties also make AFRP difficult to process during the drilling process and prone to serious entrance and exit damages. These problems seriously affect the assembly accuracy and mechanical properties of composite structures. ### Main Research Contents 1. **Cutting Mechanism Analysis**: - The paper conducts a detailed study on the cutting mechanisms of three typical drill bits (twist drill, countersink drill, spot - facing drill) when dry - drilling AFRP. - At the hole entrance, the cutting edge of the twist drill will peel and tear the uncut material, resulting in serious fuzz damage; while the countersink drill and the spot - facing drill can pre - tension the aramid fibers before cutting due to the existence of their radial rake angles, effectively reducing fuzz defects. - At the hole exit, the twist drill and the countersink drill cause exit damages respectively due to the extrusion of the tool and severe chip adhesion; in contrast, the spot - facing drill obtains the best hole quality due to the reduced thrust and the improved shearing action. 2. **Experimental Verification**: - The cutting performance and hole quality of different tools are evaluated through systematic experiments. - An auxiliary method - using bushings is introduced to effectively suppress damages, enhance the interface bonding strength, and further improve the hole quality. 3. **Micro - analysis**: - The AFRP cutting behavior under different tool geometries is analyzed on a micro - scale, revealing the interaction mechanism between the cutting edge and the composite material. ### Conclusion This research provides comprehensive information about tool performance when drilling AFRP, which is helpful for guiding process optimization to achieve the required hole quality. In particular, the spot - facing drill performs excellently in reducing entrance and exit damages, and the introduced bushing - assisted method can further improve the hole quality. ### Formula Summary - **Delamination Factor \( F_d \)**: \[ F_d=\frac{D_{\text{del}}}{D_{\text{norm}}} \] where \( D_{\text{del}} \) is the maximum diameter of the delamination area, and \( D_{\text{norm}} \) is the nominal diameter. - **Fuzz Factor \( F_f \)**: \[ F_f = \frac{A_{\text{fuzz}}}{A_{\text{norm}}} \] where \( A_{\text{fuzz}} \) is the area of the fuzz defect, and \( A_{\text{norm}} \) is the normal area of the hole. - **Tear Factor \( F_t \)**: \[ F_t=\frac{A_{\text{tear}}}{A_{\text{norm}}} \] where \( A_{\text{tear}} \) is the area of the tear defect, and \( A_{\text{norm}} \) is the normal area of the hole. Through these studies, the paper provides theoretical basis and technical support for improving the AFRP drilling quality.

Comprehensive investigation of cutting mechanisms and hole quality in dry drilling woven aramid fibre–reinforced plastic with typical tools

A New Strategy of Carbon Fiber Reinforced Plastic Drilling Evaluation Using Thermal Measurement

Investigation of Damage Reduction When Dry-Drilling Aramid Fiber-Reinforced Plastics Based on a Three-Point Step Drill

Experimental study on the hole machining process of a newly developed AFRP/Al/AFRP co-cured material: A comparative analysis of milling and drilling

Hole quality and tool wear when dry drilling of a new developed metal/composite co-cured material

Drill-milling process and novel drill-milling tool for making a hole on carbon fiber–reinforced plastics

Hole quality in longitudinal–torsional coupled ultrasonic vibration assisted drilling of carbon fiber reinforced plastics

Carbon fiber reinforced polymer in drilling: From damage mechanisms to suppression

Study on Burr Formation and Tool Wear in Drilling CFRP and Its Hybrid Composites

Understanding the Effect of Drilling Parameters on Hole Quality of Fiber-Reinforced Polymer Structures

Study on dedicated drill bit design for carbon fiber reinforced polymer drilling with improved cutting mechanism

Recent advances in drilling of carbon fiber–reinforced polymers for aerospace applications: a review

Wear behaviour of CVD diamond-coated tools in the drilling of woven CFRP composites

Influence of cutting tool design on ultrasonic-assisted drilling of fiber metal laminates

Damage mechanism of carbon fiber reinforced plastic pipe based on reverse and forward curvature drilling

Comparative analysis of wobble milling, helical milling and conventional drilling of CFRPs

Optimization of CFRP drilling process: a review

Improving hole quality of thick CFRP laminates through a laser-mechanical compound drilling process

Reducing delamination risk with response surface methodology-supported drilling analysis for Nomex® aramid fiber composites

A study on the ultrasonic vibration on the cutting performance during ultrasonic-assisted drilling of CFRP with twist and dagger drill bits

Drill bit with clip-edges based on the force control model for reducing the CFRP damage