Abstract:The natural aging (NA) behaviors within 24 h of 7050 (Al-Zn-Mg-Cu) and 5A90 (Al-Mg-Li) aluminum (Al) alloys are investigated comparatively. The strikingly different evolution rules of mechanical properties and microstructures of the above two materials are characterized using tensile strength tests and high-resolution transmission electron microscopy (HRTEM), then the mechanisms are revealed based on the analysis of differential scanning calorimetry (DSC) and the calculation of precipitation activation energy. It is found that the NA rate of 7050 Al alloy is pronounced in the initial stage (after quenching), and decreases dramatically from 0 h to 20 h of NA, resulting in remarkable evolution of the microstructures and mechanical properties. In contrary, 5A90 Al alloy is stable and the effect of NA is not evident. DSC analysis indicates that the activation energy of the initial precipitate (GP zones) for 7050 Al alloy is nearly 74.3 KJ/mol, while that of the initial precipitate (delta' phase) for 5A90 Al alloy is nearly 103.6 KJ/mol. Owing to the low activation energy, acicular GP zones precipitate in the matrix of 7050 Al alloy within the first 4 h of NA, causing a dramatic increase in strength. The precipitates continue to grow with increasing aging time, albeit at a slower rate and with reduced influence on mechanical strength. Whereas, the strength of the 5A90 Al alloy remains hardly changed due to the higher activation energy. It is noted that, for 7050 Al alloy, the NA induced decreasing of the solute atomic concentration makes the initial remarkable Portevin-Le Chatelier (PLC) effect weaken gradually with aging time. While for the 5A90 AI alloy, the PLC effect remains little changed all the time since NA phenomenon does not occur in this alloy. It is recommended that the as-quenched 7050 Al alloys should be exposed at room temperature for more than 20 h or refrigerated before practical processing.

Evolution of surface characteristics of two industrial 7xxx aluminium alloys exposed to humidity at moderate temperature

Atomic-scale study on the precipitation behavior of an Al-Zn-Mg-Cu alloy during isochronal aging

Microstructure Evolution and the Resulted Influence on Localized Corrosion in Al-Zn-Mg-Cu Alloy during Non-Isothermal Ageing

Microstructure Imaging, Precipitation Formation and Mechanical Properties: Al–Li and Al–Mg–Zn Alloys

Revisiting stress-corrosion cracking and hydrogen embrittlement in 7xxx-Al alloys at the near-atomic-scale

Different Aging Behaviors at Surface Layer and Central Region of a Die-Casting A380 Alloy During Heat Treatment

Environmental Failure Behavior Analysis of 7085 High Strength Aluminum Alloy under High Temperature and High Humidity

Correlation of microstructure with corrosion performance in high zinc 7068 aluminum alloy aged using different T6 conditions

Mechanical Properties and Microstructure Evolution of Typical Over-Aging State Al-Zn-Mg-Cu Alloy during Thermal Exposure

Investigation of the mechanisms on the abnormal features observed in thermal-mechanical testing of AA6061 under extrusion conditions

Modelling the Effect of Room Temperature Storage and Deformation on the Age-hardening Behaviour of Al-Mg-Si alloys

Corrosion Behavior and Mechanical Performance of 7085 Aluminum Alloy in a Humid and Hot Marine Atmosphere

Early-Stage Precipitation Phenomena and Composition-Dependent Hardening in Al-Mg-Si-(Cu) Alloys

Natural Aging Behaviors and Mechanisms of 7050 and 5A90 Al Alloys: A Comparative Study

Microstructural Influences Caused by Different Aging Strategies on the Strain-Dependent Damping of the High-Strength Aluminum Alloy AA7075

Effect of Solution Heat Treatment on the Microstructure and Microhardness of 7050 Aluminum Alloy

Improvement of Pitting-Corrosion Resistance of Ultrafine-Grained 7475 Al Alloy by Aging

A high-resolution characterization of surface film formed on alloys 800 and 690 exposed to chloride and thiosulfate-containing solution at 300°C

On the early stages of localised atmospheric corrosion of magnesium–aluminium alloys

Effect of Composition on Microstructural Evolution during Homogenization of 7XXX Alloys