Abstract:Traditional metal-alloy bone fixation devices provide structural support for bone repair but have limitations in actively promoting bone healing and often require additional surgeries for implant removal. In this study, we focused on addressing these challenges by fabricating biodegradable composites using poly(lactic acid) (PLA) and strontium-substituted nanohydroxyapatite (SrHAP) via melt compounding and injection molding. Various percentages of SrHAP (5, 10, 20, and 30% w/w) were incorporated into the PLA matrix. We systematically investigated the structural, morphological, thermal, mechanical, rheological, and dynamic mechanical properties of the prepared composites. Notably, the tensile modulus, a critical parameter for orthopedic implants, significantly improved from 2.77 GPa in pristine PLA to 3.73 GPa in the composite containing 10% w/w SrHAP. The incorporation of SrHAP (10% w/w) into the PLA matrix led to an increased storage modulus, indicating a uniform dispersion of SrHAP within the PLA and good compatibility between the polymer and nanoparticles. Moreover, we successfully fabricated screws using PLA composites with 10% (w/w) SrHAP, demonstrating their formability at room temperature and radiopacity when observed under X-ray microtomography (micro-CT). Furthermore, the water contact angle decreased from 93 ± 2° for pristine PLA to 75 ± 3° for the composite containing SrHAP, indicating better surface wettability. To assess the biological behavior of the composites, we conducted in vitro cell-material tests, which confirmed their osteoconductive and osteoinductive properties. These findings highlight the potential of our developed PLA/SrHAP10 (10% w/w) composites as machinable implant materials for orthopedic applications. In conclusion, our study presents the fabrication and comprehensive characterization of biodegradable composites comprising PLA and strontium-substituted nanohydroxyapatite (SrHAP). These composites exhibit improved mechanical properties, formability, and radiopacity while also demonstrating desirable biological behavior. Our results suggest that these PLA/SrHAP10 composites hold promise as machinable implant materials for orthopedic applications.

Investigations on joining of orthopaedic scaffold with rapid tooling

3D printed scaffolds for tissue engineering applications: Mechanical, morphological, thermal, in-vitro and in-vivo investigations

Investigations for tensile, compressive and morphological properties of 3D printed functional prototypes of PLA-PEKK-HAp-CS

3D Printing Surgical Implants at the Clinic: A Experimental Study on Anterior Cruciate Ligament Reconstruction

Experimental investigation of 3D printed polylactic acid and polylactic acid – hydroxyapatite composite through material extrusion technique for biomedical application

Preparation and performance of poly (vinyl alcohol)/polylactic acid/hydroxyapatite composite scaffolds based on 3D printing

Characterization of flexural and compressive behavior in polylactic acid composites for low‐cost transtibial prosthetic applications: Influence of reinforcements

Investigating the Influence of Additive Manufacturing and Ultrasonic Coating Parameters on Biopolymeric Scaffold Performance Using Response Surface Methodology

Strontium-Substituted Nanohydroxyapatite-Incorporated Poly(lactic acid) Composites for Orthopedic Applications: Bioactive, Machinable, and High-Strength Properties

Experimental investigation of PCL‐based composite material fabricated using solvent‐cast 3D printing process

Processing of Ti50Nb50−xHAx composites by rapid microwave sintering technique for biomedical applications

Investigations on friction stir spot welding to overcome bed size limits of material extrusion (MEX) 3D printers

Rapid Batch Surface Modification of 3D-Printed High-Strength Polymer Scaffolds for Enhanced Bone Regeneration In Vitro and In Vivo

Fabrication of Biocompatible Composites of Poly(lactic acid)/Hydroxyapatite Envisioning Medical Applications

Biocompatibility and mechanical behaviour of three-dimensional scaffolds for biomedical devices: process–structure–property paradigm

On fabrication of acrylonitrile butadiene styrene-zirconium oxide composite feedstock for 3D printing-based rapid tooling applications

3D printing of HA / PCL composite tissue engineering scaffolds

On 3D printed thermoresponsive PCL-PLA nanofibers based architected smart nanoporous scaffolds for tissue reconstruction

Investigation of Fused Deposition Modelling Process Parameters in 3D Printing for Composite Material (Poly Lactic Acid and Banana Fibre)

Mechanical and biological behaviour of additive manufactured biomimetic biodegradable orthopaedic cortical screws

Experimental investigations on polydopamine coated poly lactic acid based biomaterial fabricated using 3D printing for orthopedic applications