Effective improvement of anti-tracking of addition-cure liquid silicone rubber via charge dissipation of fluorosilane-grafted silica

Chixin Xie,Xuejun Lai,Hongqiang Li,Xingrong Zeng
DOI: https://doi.org/10.1016/j.polymdegradstab.2019.06.014
IF: 5.204
2019-09-01
Polymer Degradation and Stability
Abstract:<p>Improving the anti-fouling and anti-tracking of silicone rubber (SR) is significant to enlarge its application in the field of outdoor high voltage insulation. In this work, fluorosilane-grafted silica (F–SiO<sub>2</sub>) was prepared by the grafting reaction of silica with perfluorooctyltriethoxysilane. Inclined-plane test (IP test), surface potential decay test, plasma irradiation, XPS and SEM were applied to study the effect of F–SiO<sub>2</sub> on the anti-tracking of addition-cure liquid silicone rubber (ALSR). The results demonstrated that F–SiO<sub>2</sub> postponed the occurrence of intensive arc discharge and reduced arc discharge on ALSR surface. The anti-plasma irradiation and anti-tracking of ALSR were remarkably enhanced. When F–SiO<sub>2</sub> content was 1 phr, ALSR/F–SiO<sub>2</sub> passed the 1A4.5 kV IP test and the erosion mass was only 0.22 wt%. Moreover, the mechanical properties and hydrophobicity of ALSR were improved. Surface potential decay test showed that F–SiO<sub>2</sub> could dissipate charges. Combining its excellent anti-plasma irradiation, it was revealed that F–SiO<sub>2</sub> dissipated the injected charges and diminished the density of charges in ALSR during the arc discharge, which reduced the damage of charges to ALSR chains and suppressed the arc discharge. Therefore, the anti-tracking of ALSR was enhanced.</p>
polymer science
What problem does this paper attempt to address?