Investigation into Influence of SiO2 Mass Fraction on Coating Performance of RTV Silicone Rubber Based on Inclined Plane Test

YANG Cui-ru,JIA Zhi-dong

DOI: https://doi.org/10.3969/j.issn.1007-290X.2010.09.006

2010-01-01

Abstract:To solve the problems of poor adhesion and easy scratching while applying coating of room temperature vulcanization(RTV) silicone rubber,the use of silica is proposed to improve the mechanical strength of silicone rubber as well as the material's resistance to electrical tracking and erosion.Therefore,combined with the concept of thermal conductivity,the influence of silica on performance of RTV silicone rubber is investigated by inclined plane test.High-precision AC tracking tester developed by Institute of Electrical and Electronic Equipment,Xi'an Jiaotong University is used in the test together with independently developed multiple leakage current real-time monitoring and acquisition device,so as to test the three prepared RTV silicone rubber coating specimens(only adding silica,mass fractions thereof being 20%,30%,50%) according to GB/T 6553-2003 Test Methods for Evaluating Resistance to Tracking and Erosion of Electrical Insulating Materials Used under Severe Ambient Conditions.It is concluded that the higher the mass fraction of silica,the greater the thermal conductivity of silicone rubber,the easier the heat transfer,and the stronger the resistance to tracking and electrical arc erosion;when reaching the critical state that actuates the overcurrent protection,the silicone rubber specimen with high silica content and large thermal conductivity has greater eroded area and depth than the specimen with low silica content;the increase of silica filler slows down the hydrophobicity recovery process of eroded silicone rubber.