A cross-linking density method study of the effect of a silane coupling agent on the performance of room temperature vulcanized(RTV) silicone rubber

S. Qing

Abstract:The cross-linking density method was used to investigate the effects of a coupling agent on the mechanical properties and the high and low temperature performance of silica-enhanced hydroxyl-terminated phenylsiloxane rubber.Mechanical properties,SEM,cross-linking density,DSC,DMA,and TGA analysis all showed that the chemical cross-linking density ratio was the greatest when the mass fraction of γ-aminopropyltriethoxysilane(KH550) was 6 parts per hundreds of hydroxyl-terminated phenylsiloxane rubber,which resulted in room temperature vulcanized silicone rubber with the highest tensile properties,as well as the optimum interface adhesion between silica and the silicone rubber.Meanwhile,the lower glass transition temperature,which resulted from the decrease in the physical cross-linking density ratio,indicated the improvement of the low temperature resistance of the silicone rubber.The increase in the chemical cross-linking density ratio showed that the heat resistance of RTV silicone rubber was improved.

Materials Science