Improvement of Interface Adhesion Property of Contaminated Rtv Silicone Rubber by Plasma Jet

J. Li,S. Li,R. Zhang

DOI: https://doi.org/10.1049/icp.2022.0090

2021-01-01

Abstract:Room Temperature Vulcanized (RTV) Silicone Rubber is widely used in electrical power system to improve insulation performance of the porcelain insulator and glass insulator. After long-time running, RTV coatings get contaminated, aged, and even peel off, needing to be recoated. The inorganic contaminants accumulate and embed into the original RTV coating, causing adverse effect on the recoating process. In this article, plasma treatment was used to process contaminated RTV coating while the contaminants were not removed. Water boiling test and swelling test were used to evaluate interfacial adhesion properties. Microscopic morphology and internal structure of recoating interface were studied by Scanning electron microscopy (SEM) and Computed tomography (CT). The chemical functional groups and element composition were studied by Fourier transform infrared (FTIR) and X-ray photoelectron spectroscopy (XPS). After plasma treatment, the blister area and peeling area on the samples during water boiling test and swelling test became smaller. Microscopic experiments show that the boundary of recoating interface became less clear, the number of voids at the interface decreased, more low molecular weight siloxanes accelerated to the contaminated layer and silicon atoms were bonded to more oxygen atoms, indicating that plasma treatment can improve the adhesion properties of contaminated RTV.