Abstract:Antimony sulfide thin films of thickness ≈500 nm have been deposited on glass slides from chemical baths constituted with SbCl3 and sodium thiosulfate. Smooth specularly reflective thin films are obtained at deposition temperatures from −3 to 10 °C. The differences in the film thickness and improvement in the crystallinity and photoconductivity upon annealing the film in nitrogen are presented. These films can be partially converted into a solid solution of the type Sb2SxSe3−x, detected in X-ray diffraction, through heating them in contact with a chemically deposited selenium thin film. This would decrease the optical band gap of the film from ≈1.7 eV (Sb2S3) to ≈1.3 eV for the films heated at 300 °C. Similarly, heating at 300 °C of sequentially deposited thin film layers of Sb2S3–Ag2Se, the latter also from a chemical bath at 10 °C results in the formation of AgSb(S/Se)2 with an optical gap of ≈1.2 eV. All these thin films have been integrated into photovoltaic structures using a CdS window layer deposited on 3 mm glass sheets with a SnO2:F coating (TEC-15, Pilkington). Characteristics obtained in these cells under an illumination of 850 W/m2 (tungsten halogen) are as follows: SnO2:F–CdS–Sb2S3–Ag(paint) with open circuit voltage (Voc) 470 mV and short circuit current density (Jsc) 0.02 mA/cm2; SnO2:F–CdS–Sb2S3–CuS–Ag(paint), Voc≈460 mV and Jsc≈0.4 mA/cm2; SnO2:F–CdS–Sb2SxSe3−x–Ag(paint), Voc≈670 mV and Jsc≈0.05 mA/cm2; SnO2:F–CdS–Sb2S3–AgSb(S/Se)2–Ag(paint), Voc≈450 mV and Jsc≈1.4 mA/cm2. We consider that the materials and the deposition techniques reported here are promising toward developing ‘all-chemically deposited solar cell technologies.’

Preparation of AlSb film by screen printing and sintering method

Alsb Thin Films Prepared By Dc Magnetron Sputtering And Annealing

Microstructural and Optical Properties of Sb2S3 Film Thermally Evaporated from Antimony Pentasulfide and Efficient Planar Solar Cells

Structure, Morphology, and Photoelectric Performances of Te-Sb 2 Se 3 Thin Film Prepared via Magnetron Sputtering.

Pulsed laser deposition of antimony selenosulfide thin film for efficient solar cells

Aqueous-Solution-Based Approach Towards Carbon-Free Sb2 S3 Films for High Efficiency Solar Cells.

In Situ Sulfurization to Generate Sb2(Se1 − Xsx)3 Alloyed Films and Their Application for Photovoltaics

Mechanistic Study of the Transition from Antimony Oxide to Antimony Sulfide in the Hydrothermal Process to Obtain Highly Efficient Solar Cells.

Structure, Morphology, and Photoelectric Performances of Te-Sb<sub>2</sub>Se<sub>3</sub>Thin Film Prepared via Magnetron Sputtering

Study of Sb2Se3/Al interface affected by oxygen exposure

Structure, Morphology, and Photoelectric Performances of Te-Sb<sub>2</sub>Se<sub>3</sub> Thin Film Prepared via Magnetron Sputtering

Synthesis and Characterization of Hydrazine Solution Processed Cu12Sb4S13 Film

Solution‐Processed Compact Sb 2 S 3 Thin Films by a Facile One‐Step Deposition Method for Efficient Solar Cells

Solution Processed AgSbS2 Film for Efficient Planar Heterojunction Solar Cells

Antimony Doping of CsBi 3 I 10 for Tailoring the Film Morphology and Defects toward Efficient Lead-Free Thin-Film Solar Cells

Antimony sulfide thin films in chemically deposited thin film photovoltaic cells

Single-source Thermal Evaporation Converts Anion Controllable Sb 2 (s,se) 3 Film for Fabricating High-Efficiency Solar Cell

Two-stage co-evaporated CuSbS2 thin films for solar cells

Solution‐Processed Compact Sb2S3 Thin Films by a Facile One‐Step Deposition Method for Efficient Solar Cells

Sputtering Al2O3 as an effective interface layer to improve open-circuit voltage and device performance of Sb2Se3 thin-film solar cells

Direct Solution Deposition of Device Quality Sb2S3-xSex Films for High Efficiency Solar Cells