Annealing Treatment Methods and Mechanisms for Refining Mixed and Coarse Grains in a Solution Treatment Nickel‐Based Superalloy

Ming-Song Chen,Guan-Qiang Wang,Hong-Bin Li,Yong-Cheng Lin,Zong-Huai Zou,Yan-Yong Ma
DOI: https://doi.org/10.1002/adem.201900558
IF: 3.6
2019-08-02
Advanced Engineering Materials
Abstract:<p>The annealing treatment methods and mechanisms for refining deformed mixed and coarse grains in a solution treatment nickel‐based superalloy are investigated. The deformed mixed and coarse grains are obtained by hot compression tests. The single‐stage annealing tests are done firstly, and it is found that the mixed and coarse grains are hardly refined to about 10 μm by a direct annealing at 980 °C due to lack of δ phase. Then, two‐stage annealing tests, in which the deformed sample is firstly heated to 900 °C for 12 h for precipitating some δ phases, and then reheated to 980 °C for a recrystallization annealing treatment (RT), are designed. It is found that the recrystallization is still not complete although a long time RT has been done. The main reason is that the distances between adjacent δ phases precipitating during direct aging are so small that the recrystallization nuclei are hard to form. So, three‐stage annealing tests including a pre‐recrystallization annealing treatment (PRT) at 980 °C, an aging annealing treatment (AT) at 900 °C and a RT at 980 °C, are designed. It is found that PRT has a favorable influence on the refinement of mixed and coarse grains during the subsequent AT and RT. The mixed and coarse grains can be refined after the three‐stage annealing treatment of 980 °C × 3 min/WQ + 900 °C × 12 h/WQ + 980 °C × 120 min/WQ.</p><p>This article is protected by copyright. All rights reserved.</p>
materials science, multidisciplinary
What problem does this paper attempt to address?