Abstract:PURPOSE The clinical failures of zirconia dental restorations are often caused by extrinsic artifacts introduced by processing. The aim of this study was to investigate the micro-defects and residual stresses generated during the multistep process of zirconia dental restorations. MATERIALS AND METHODS Thermal spray granulated 3Y-TZP powders were dry pressed by two tools exhibiting distinctly different Young's moduli, cold isostatic pressed (CIP-ed), and pressure-less fully sintered. The green bodies pressed by a stiff tool were treated with different procedures: direct milling (green milling) followed by fully sintering; half-sintering and milling (raw milling) with or without fully sintering; and fully sintering followed by grinding. The fully sintered 3Y-TZP crowns were clinically adjusted using both a diamond bur and SiC bur, respectively. Phase composition and microstructure of the pressed, milled, and ground surfaces were studied by XRD and SEM. RESULTS Tetragonal phase was the main phase of all detected 3Y-TZP specimens. Excessive residual stresses introduced by raw milling and grinding were confirmed by a strained T (111) peak, monoclinic phase, and obviously changed I(002)t /I(200)t ratio. The residual stresses would form a compressive stress layer, while it was too shallow to inhibit crack propagation even for ground specimens. Large voids with high-coordination numbers were the common packing micro-defects. Once formed, they were barely healed by CIP-ing and sintering. A stiff pressing tool was confirmed to be useful for reducing the surface packing voids. Milling removed the surface voids, but was no help for the interior ones. Raw milling introduced more serious chippings, most originating from the existing packing voids, than green milling due to its brittle failure and was less recommended for production. Grinding dense 3Y-TZP caused surface grain refinement and much more severe micro-defects, especially when clinical adjustment was applied by diamond bur compared to SiC bur. CONCLUSIONS Micro-defects and residual stresses are introduced and accumulated through the entire production chain and determine the final microstructure of zirconia dental restorations. Several procedural improvements are offered and expected to reduce processing micro-defects.

Surface Roughness Analysis of Zirconia Dental Restoration Manufactured Through CNC Milling Machine

Effect of Machining Method and Margin Design on the Accuracy and Margin Quality of Monolithic Zirconia Crowns

Influence of Restoration Thickness and Resin Cement on Translucency and Color of Different Types of Monolithic Zirconia and Lithium Disilicate Ceramic

The Surface Roughness of Contemporary Indirect CAD/CAM Restorative Materials That Are Glazed and Chair-Side-Finished/Polished

Evaluation of Zirconia Surface Roughness after Different Surface Treatment with Sandblasting, Hydrofluoric Acid Etching, and Combination Treatment

The influence of different surface treatments on the topography of CAD/CAM zirconia implant surface

A review on surface texturing of zirconia ceramics for dental applications

Effect of Milling Speed on the Properties of Zirconia Restorations

Analysis of a Regression Model for Creating Surface Microgeometry after Machining Zirconia YML Used for Dental Application

Evaluation of Surface Roughness of Translucent Zirconia After Applying Nd:YAG and CO2 Lasers: An In Vitro Study

Zirconia Dental Implants: A Closer Look at Surface Condition and Intrinsic Composition by SEM-EDX

Evaluation of the Feasibility of NaCaPO4-Blended Zirconia as a New CAD/CAM Material for Dental Restoration

Effect of Low-Temperature Degradation, Ph-Cycling and Simulated Tooth Brushing on Surface Roughness, Topography, and Polish Retention of Yttrium-Stabilized Tetragonal Zirconia

Surface Properties of Dental 3Y-TZP with Different Treatments

Effect of Multistep Processing Technique on the Formation of Micro-Defects and Residual Stresses in Zirconia Dental Restorations.

The Application Potential of Self-Glazed Zirconia Crowns Confirmed by Easy Grinding and Polishing of the Enamel-Like Surface

Dental zirconia fabricated by stereolithography: Accuracy, translucency and mechanical properties in different build orientations

Performance of Stereolithography and Milling in Fabricating Monolithic Zirconia Crowns with Different Finish Line Designs.

Surface roughness of nanofill and nanohybrid composite resin and ormocer-based tooth-colored restorative materials after several finishing and polishing procedures

In vitro surface characteristics and impurity analysis of five different commercially available dental zirconia implants

Surface quality evaluation through 3D profilometry of dental restoration performed in a clinical simulated environment