Abstract:Metal additive manufacturing (AM) processes, such as laser powder bed fusion (L-PBF), can yield high-value parts with unique geometries and features, substantially reducing costs and enhancing performance. However, the material properties from L-PBF processes are highly sensitive to the laser processing conditions and the resulting dynamic temperature fields around the melt pool. In this study, we develop a methodology to measure thermal gradients, cooling rates, and solidification velocities during solidification of refractory alloy C103 using in situ high-speed infrared (IR) imaging with a high frame rate of approximately 15,000 frames per second (fps). Radiation intensity maps are converted to temperature maps by integrating thermal radiation over the wavelength range of the camera detector while also considering signal attenuation caused by optical parts. Using a simple method that assigns the liquidus temperature to the melt pool boundary identified ex situ, a scaling relationship between temperature and the IR signal was obtained. The spatial temperature gradients (dT/dx), heating/cooling rates (dT/dt), and solidification velocities (R) are resolved with sufficient temporal resolution under various laser processing conditions, and the resulting microstructures are analyzed, revealing epitaxial growth and nucleated grain growth. Thermal data shows that a decreasing temperature gradient and increasing solidification velocity from the edge to the center of the melt pool can induce a transition from epitaxial to equiaxed grain morphology, consistent with the previously reported columnar to equiaxed transition (CET) trend. The methodology presented can reduce the uncertainty and variability in AM and guide microstructure control during AM of metallic alloys.

Limits and solutions in processing pure Cu via selective laser melting using a high-power single-mode fiber laser

Intentional Oxidation and Laser Remelting of Highly Reflective Pure Cu for Its High‐Quality Additive Manufacturing

Power Density Distribution for Laser Additive Manufacturing (SLM): Potential, Fundamentals and Advanced Applications

Selective Laser Melting of High Relative Density and High Strength Parts Made of Minor Surface Oxidation Treated Pure Copper Powder

Process of Pure Copper Fabricated by Selective Laser Melting (SLM) Technology under Moderate Laser Power with Re-Melting Strategy

Selective laser melting of CuCrZr alloy: processing optimisation, microstructure and mechanical properties

Selective laser melting 316L/CuSn10 multi-materials: Processing optimization, interfacial characterization and mechanical property

Laser based post processing of additive manufactured metal parts

The Use of Sacrificial Graphite-like Coating to Improve Fusion Efficiency of Copper in Selective Laser Melting

Effect of Process Parameters on Residual Stresses, Distortions, and Porosity in Selective Laser Melting of Maraging Steel 300

Review of selective laser melting: Materials and applications

Effect of Process Parameters on the Microstructure and Properties of Cu–Cr–Nb–Ti Alloy Manufactured by Selective Laser Melting

Resolving thermal gradients and solidification velocities during laser melting of a refractory alloy

Parametric analysis of the selective laser melting process

Research on High Layer Thickness Fabricated of 316L by Selective Laser Melting

Understanding of process and material behaviours in additive manufacturing of Invar36/Cu10Sn multiple material components via laser-based powder bed fusion

Area melting with multi-laser arrays to increase build rate for metal powder bed fusion additive manufacturing

Spiral growth selective laser melting of axisymmetric objects from Cu-Ni–Sn alloy powder: a mass rate efficiency and physical properties study

Numerical Modelling and Experimental Validation of Selective Laser Melting Processes Using a Custom Argon Chamber Setup for 316L Stainless Steel and Ti6AI4V

Capillary effects and consolidation kinetics during selective laser melting of 316L powder