Abstract:Selective Laser Melting (SLM), as an emerging additive manufacturing technology, has attracted increasing attention in the field of copper alloys. To reduce the production cost of SLM-formed copper alloys and enhance the mechanical properties of the alloy materials, this work uses CuSn10 alloy powder prepared by the water atomization method as the raw material, and optimizes the process parameters during SLM through the response surface and variance analysis methods, to prepare almost fully dense CuSn10 alloy blocks. By adding a certain proportion of WC hard particles to the CuSn10 alloy powder, this work investigates the microstructural evolution and mechanical properties of the specimens before and after the addition of particles, and explores the regularity of the influence of the addition of hard particles on the microstructural evolution and mechanical properties of the formed parts by comparing the experimental results. The results show that the SLM-formed CuSn10 specimens exhibit a fine-grained microstructure composed of cellular and dendritic structures. The addition of WC hard particles changes the microstructure of the composite material, eliminating the preferred growth inside the specimens, and due to the effects of hard carbide phase, heterogeneous nucleation and dispersion strengthening, a more refined and uniform microstructure is achieved. The performance of the specimens also varies considerably, with the Vickers hardness increasing from 155HV to 215HV, the ultimate tensile strength increasing from 578MPa to 625MPa, and the elongation at fracture decreasing from 15% to 5%. The wear resistance and corrosion resistance show the same trend, with the wear resistance and corrosion resistance of the composite material first decreasing and then increasing as the WC content increases, reaching the best when the content is 10%. It can be seen that by reasonably adjusting the proportion of the WC reinforcement phase in the copper-based composite material, the hardness and wear resistance of the SLM-formed CuSn10 alloy can be significantly improved, expanding the engineering application prospects of copper alloy parts in extreme working conditions such as wear and corrosion.

Selective laser melting 316L/CuSn10 multi-materials: Processing optimization, interfacial characterization and mechanical property

Dual interfacial characterization and property in multi-material selective laser melting of 316L stainless steel and C52400 copper alloy

A Facile and Sustainable Integrated Fabrication Strategy for Multi-Performance 316l Stainless Steel

The impact of interfacial characteristics on the interfacial properties of 316 L/CuSn10 multi-material manufactured by laser powder bed fusion

Microstructure and mechanical properties of CuCrZr/316L hybrid components manufactured using selective laser melting

Simultaneous strength and ductility enhancements of high thermal conductive Ag7.5Cu alloy by selective laser melting

Selective Laser Melting of Duplex Stainless Steel 2205: Effect of Post-Processing Heat Treatment on Microstructure, Mechanical Properties, and Corrosion Resistance

Effects of WC Particles on the Microstructure and Properties of Copper Matrix Composites by Selective Laser Melting

Tensile Properties of Selective Laser Melted 316L Stainless Steel

Processing Technologies and Properties of Cu-10Sn Formed by Selective Laser Melting Combined with Heat Treatment

Selective laser melting of CuCrZr alloy: processing optimisation, microstructure and mechanical properties

Selective laser melting of Al-3.48Cu-2.03Si-0.48Sc-0.28Zr alloy: Microstructure evolution, properties and metallurgical defects

Enhancing the interface strength of additively manufactured 316 L/CuSn10 bimetallic components through heterogeneous microstructures

Selective Laser Melting of High Relative Density and High Strength Parts Made of Minor Surface Oxidation Treated Pure Copper Powder

Selective Laser Melting of Cu–10Sn–0.4P: Processing, Microstructure, Properties, and Brief Comparison with Additively Manufactured Cu–10Sn

Hierarchical microstructure and strengthening mechanism of Cu-36.8Fe alloy manufactured by selective laser melting

Pure copper components fabricated by cold spray (CS) and selective laser melting (SLM) technology

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility

Study on performance optimization of 316L stainless steel parts by High-Efficiency Selective Laser Melting

Characteristics of Metal Specimens Formed by Selective Laser Melting: A State-of-the-Art Review

Microstructural and mechanical characterization of steel-copper composite structures fabricated by laser powder bed fusion and induction melting