Abstract:In this study, polyurethane (PU) foams were manufactured using kraft lignin and castor oil as bio-based polyols by replacing 5–20 wt% and 10–100 wt% of conventional polyol, respectively. To investigate the effects of unmodified bio-based polyols on PU foam production, reactivity and morphology within PU composites was analyzed as well as mechanical and thermal properties of the resulting foams. Bio-based PU foam production was carried out after characterizing the reagents used in the foaming process (including hydroxyl group content, molecular weight distribution, and viscosity). To compare the resulting bio-based PU foams, control foam were produced without any bio-based polyol under the same experimental conditions. For lignin-incorporated PU foams, two types, LPU and lpu, were manufactured with index ratio of 1.01 and 1.3, respectively. The compressive strength of LPU foams increased with lignin content from 5 wt% (LPU5: 147 kPa) to 20 wt% (LPU20: 207 kPa), although it remained lower than that of the control foam (PU0: 326 kPa). Similarly, the compressive strength of lpu foams was lower than that of the control foam (pu0: 441 kPa), with values of 164 kPa (lpu5), 163 kPa (lpu10), 167 kPa (lpu15), and 147 kPa (lpu20). At 10 wt% lignin content, both foams (LPU10 and lpu10) exhibited the smallest and most homogenous pore sizes and structures. For castor oil-incorporated PU foams with an index of 1.01, denoted as CPU, increasing castor oil content resulted in larger cell sizes and void fractions, transitioning to an open-cell structure and decreasing the compressive strength of the foams from 284 kPa (CPU10) to 23 kPa (CPU100). Fourier transform infrared (FT-IR) results indicated the formation of characteristic urethane linkages in PU foams and confirmed that bio-based polyols were less reactive with isocyanate compared to traditional polyol. Thermogravimetric analysis (TGA) showed that incorporating lignin and castor oil affected the thermal decomposition behavior. The thermal stability of lignin-incorporated PU foams improved as the lignin content increased with char yields increasing from 11.5 wt% (LPU5) to 15.8 wt% (LPU20) and from 12.4 wt% (lpu5) to 17.5 wt% (lpu20). Conversely, the addition of castor oil resulted in decreased thermal stability, with char yields decreasing from 10.6 wt% (CPU10) to 4.2 wt% (CPU100). This research provides a comprehensive understanding of PU foams incorporating unmodified biomass-derived polyols (lignin and castor oil), suggesting their potential for value-added utilization as bio-based products.

Lignin-Based Polyurethanes: Opportunities for Bio-Based Foams, Elastomers, Coatings and Adhesives

Lignin‐Based Polyurethane: Recent Advances and Future Perspectives

The extraction of polyol for the synthesis of lignin-based polyurethane coatings – a review

RECENT ADVANCES ON LIGIN-DERIVED POLYURETHANE POLYMERS

Preparation of Mechanically Robust Bio-Based Polyurethane Foams Using Depolymerized Native Lignin

Development and Application of a Lignin-Based Polyol for Sustainable Reactive Polyurethane Adhesives Synthesis

Effect of Liquefied Lignin Content on Synthesis of Bio-based Polyurethane Foam for Oil Adsorption Application

Investigation of bio-based rigid polyurethane foams synthesized with lignin and castor oil

Modification of Renewable Resources-Lignin-by Three Chemical Methods and Its Applications to Polyurethane Foams

Lignin Polyurethane Aerogels: Influence of Solvent on Textural Properties

Highly Resilient Lignin-Containing Polyurethane Foam

The Use of Lignin As Cross-linker for Polyurethane Foam for Potential Application in Adsorbing Materials

Research Status of Lignin-Based Polyurethane and Its Application in Flexible Electronics

New Kinds of Lignin/non-Isocyanate Polyurethane Hybrid Polymers: Facile Synthesis, Smart Properties and Adhesive Applications

Synthesis and Characterizations of Eco-Friendly Organosolv Lignin-Based Polyurethane Coating Films for the Coating Industry

Use of lignin in polyurethane-based structural wood adhesives

Successive organic solvent fractionation and homogenization of technical lignin for polyurethane foam with high mechanical performance

Solvent-free synthesis of high-performance polyurethane elastomer based on low-molecular-weight alkali lignin

Bio-based polyurethane foam preparation employing lignin from corn stalk enzymatic hydrolysis residues

Fractionated lignin as a polyol in polyurethane fabrication

Research Development of Lignin Chemical Modification and Its Application on the Synthesis of Polyurethane