Investigation of bio-based rigid polyurethane foams synthesized with lignin and castor oil

Hyeon Jeong Kim,Xuanjun Jin,Joon Weon Choi

DOI: https://doi.org/10.1038/s41598-024-64318-8

IF: 4.6

2024-06-13

Scientific Reports

Abstract:In this study, polyurethane (PU) foams were manufactured using kraft lignin and castor oil as bio-based polyols by replacing 5–20 wt% and 10–100 wt% of conventional polyol, respectively. To investigate the effects of unmodified bio-based polyols on PU foam production, reactivity and morphology within PU composites was analyzed as well as mechanical and thermal properties of the resulting foams. Bio-based PU foam production was carried out after characterizing the reagents used in the foaming process (including hydroxyl group content, molecular weight distribution, and viscosity). To compare the resulting bio-based PU foams, control foam were produced without any bio-based polyol under the same experimental conditions. For lignin-incorporated PU foams, two types, LPU and lpu, were manufactured with index ratio of 1.01 and 1.3, respectively. The compressive strength of LPU foams increased with lignin content from 5 wt% (LPU5: 147 kPa) to 20 wt% (LPU20: 207 kPa), although it remained lower than that of the control foam (PU0: 326 kPa). Similarly, the compressive strength of lpu foams was lower than that of the control foam (pu0: 441 kPa), with values of 164 kPa (lpu5), 163 kPa (lpu10), 167 kPa (lpu15), and 147 kPa (lpu20). At 10 wt% lignin content, both foams (LPU10 and lpu10) exhibited the smallest and most homogenous pore sizes and structures. For castor oil-incorporated PU foams with an index of 1.01, denoted as CPU, increasing castor oil content resulted in larger cell sizes and void fractions, transitioning to an open-cell structure and decreasing the compressive strength of the foams from 284 kPa (CPU10) to 23 kPa (CPU100). Fourier transform infrared (FT-IR) results indicated the formation of characteristic urethane linkages in PU foams and confirmed that bio-based polyols were less reactive with isocyanate compared to traditional polyol. Thermogravimetric analysis (TGA) showed that incorporating lignin and castor oil affected the thermal decomposition behavior. The thermal stability of lignin-incorporated PU foams improved as the lignin content increased with char yields increasing from 11.5 wt% (LPU5) to 15.8 wt% (LPU20) and from 12.4 wt% (lpu5) to 17.5 wt% (lpu20). Conversely, the addition of castor oil resulted in decreased thermal stability, with char yields decreasing from 10.6 wt% (CPU10) to 4.2 wt% (CPU100). This research provides a comprehensive understanding of PU foams incorporating unmodified biomass-derived polyols (lignin and castor oil), suggesting their potential for value-added utilization as bio-based products.

multidisciplinary sciences

What problem does this paper attempt to address?

This paper aims to study the influence of using unmodified biomass - derived polyols (such as lignin and castor oil) to partially replace traditional polyether polyols in the preparation of polyurethane (PU) foams. Specifically, the research objectives include:

1. **Reactivity and Morphology Analysis**: Evaluate the influence of unmodified biomass - derived polyols on the reactivity and morphological characteristics during the PU foam production process.
2. **Mechanical and Thermal Properties**: Analyze the influence of biomass - derived polyols on the mechanical properties (such as compressive strength) and thermal properties (such as thermal stability) of PU foams.
3. **Detailed Description of the Experimental Process**: Record in detail the characterization methods of biomass - derived polyols used in the foam manufacturing process, including parameters such as hydroxyl content, molecular weight distribution, and viscosity.

Through these studies, the authors hope to provide basic information on the preparation of PU foams using unmodified biomass - derived polyols and explore their potential application value as bio - based products.