Abstract:Phosphogypsum (PG) is a kind of industrial solid waste with high impurity content and low utilization rate. In this study, α-hemihydrate gypsum (α-HH) was synthesized from PG in H3PO4–H2O solution (wet-process phosphoric acid solution and phosphoric acid solution) under atmospheric pressure. The crystal morphology of α-HH was controlled by adding F and Al compound regulators, and the mechanical properties of α-HH were improved. The difference of α-HH synthesized by PG with different qualities was analyzed, and the mechanism of α-HH morphology was studied by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and energy-dispersive spectroscopy (EDS). Results showed that in the wet-process phosphoric acid solution, α-HH synthesized from white PG (by H3PO4–H2SO4 two-step method) had better whiteness, purity, and mechanical properties compared with that from industrial PG, and the performance indexes of the α-HH products met the requirements of α50 grade in JC/T 2038–2010 α-high-strength gypsum in China and have a good commercial application prospect. Moreover, in the phosphoric acid solution, the average diameter of the α-HH crystal increased from 8.1 µm to 54.8 µm, the average aspect (L/D) ratio decreased from 32.65 to 0.52, and the induction period and growth period of the α-HH crystal were prolonged with the increase in regulator dosage. F− and Al3+ ions were preferred to adsorb on the crystal faces. The growth of the crystal parallel to c-axis (200), (020), and (400) was inhibited, and the morphology of the α-HH crystal changed from whisker to short column. When the dosage of the regulator was 1.1 %, the 2 h bending strength of the α-HH product was 6.56 MPa, and the drying compressive strength was 52.4 MPa. This study provides a new technique and method for the synthesis of high-strength α-HH products from PG.

Utilization of hemihydrate phosphogypsum for the preparation of porous sound absorbing material

Improving the mechanical property and water resistance of β-hemihydrate phosphogypsum by incorporating ground blast-furnace slag and steel slag

Improving mechanical properties of hemihydrate phosphogypsum via alkali-activated mineral admixtures

Effect of calcium sulphoaluminate cement on mechanical strength and waterproof properties of beta-hemihydrate phosphogypsum

Study on the Mechanical Properties, Microstructure and Hydration Mechanism of Phosphogypsum-Based Geopolymer Cement with Added Micron-Sized Silica Particles

Low cost and high efficiency utilization of hemihydrate phosphogypsum: Used as binder to prepare filling material

Improvement of the mechanical properties of beta-hemihydrate phosphogypsum by incorporating wet-ground low-calcium fly ash slurries

Mechanical properties and soluble phosphorus solidification mechanism of a novel high amount phosphogypsum-based mortar

Effect of Synergistic Modification of Building Materials Based on α-Hemihydrate Phosphogypsum by Portland Cement/H-PDMS on Water Resistance

Study on physical and chemical characteristics of β-hemihydrate phosphogypsum

Eco-friendly, high-toughness gypsum prepared using hemihydrate phosphogypsum, fly ash, and glass fibers: Characterization and environmental impacts

Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum

Utilization of phosphogypsum to synthesize α-hemihydrate gypsum in H3PO4–H2O solution

Low-Energy Consumption Preparation of Fine Waterproof Cementitious Material with High-Volume Phosphogypsum

Properties of Cemented Filling Materials Prepared from Phosphogypsum-Steel Slag-Blast-Furnace Slag and Its Environmental Effect

Preparation of Foamed Phosphogypsum Lightweight Materials by Incorporating Cementitious Additives

Utilization of untreated-phosphogypsum as filling and binding material in preparing grouting materials

Influence of calcination and GGBS addition in preparing β-hemihydrate synthetic gypsum from phosphogypsum

Study on the improvement of the waterproof and mechanical properties of hemihydrate phosphogypsum-based foam insulation materials

Development and optimization of phosphogypsum-based geopolymer cement