Abstract:Electrolytic manganese residue (EMR) is a solid filter residue obtained from manganese carbonate ore during the production of metal manganese. A potential avenue towards large-scale utilisation of EMR is its use in cement preparation. However, the preparation of cement materials using EMR requires high-temperature calcination. In this study, the thermal properties and pyrolysis kinetics of belite–calcium sulfoaluminate cement raw meal were systematically studied using a multiple-heating-rate method based on thermogravimetric analysis and a kinetic model. The kinetic and thermodynamic parameters was studied using non-isothermal Flynn–Wall–Ozawa (FWO), Kissinger–Akahira–Sunose (KAS), Friedman and Kissinger methods. The results showed that from 30 to 1300°C, the pyrolysis reaction of cement raw meal was mainly divided into four steps: the crystalline water removal from calcium sulphate dihydrate and bauxite, the ammonia nitrogen removal from ammonium salts and the calcium sulphate crystal transformation; the decomposition of calcium carbonate and carbon-containing organic matter; the sulphate and carbonate substance decomposition and the clinker mineral phase formation. The average activation energies calculated when using the non-isothermal FWO, KAS, Friedman and Kissinger methods were 244.49, 240.7, 239.24 and 380.60 kJ/mol and the average pre-exponential factors were 1.75 × 10 20 , 3.65 × 10 20 , 7.11 × 10 21 and 1.55 × 10 13 s −1 , respectively. Herein, the pyrolysis kinetics of the cement raw meal was divided into two main stages: In stage 1 ( α : 0.15–0.8, 524°C–754°C), the mechanism of P2/3 accelerated nucleation in the Mampel Power rule, and the reaction mechanism function was G( α )= α 3/2 . In stage 2 ( α : 0.80–0.95, 754°C–1165°C), during the local conversion of α = 0.2–0.8, when α was <0.5, the chemical reaction mechanism of the R3 phase boundary was noted and the mechanism function was G( α ) = 1 − (1− α ) 1/3 ; however, when α was >0.5, a random nucleation and subsequent growth mechanism of A6 was noted and the mechanism function was G( α ) = [−ln(1 − α )] 2/3 .

Study on kinetics of the pyrolysis process of aluminum sulfate

Kinetics of the multistage dehydration of aluminum sulfate hydrate

Effect of Aluminium Sulfate on Carbothermal Reduction of Phosphorite in a Fluidized Bed

Kinetics for Thermal Decomposition of Anhydrous Aluminum Sulfate Powder Composed of Single Crystal Rhombohedrons in Shape.

Thermodynamics and kinetics of the carbothermal reduction of aluminum sulfate

The Preparation of Aluminum Hydroxide from High-Alumina Gangue Desilication Residues Based on Soda Lime Sintering Method

Extraction of alumina from aluminum dross by a non-hazardous alkaline sintering process: Dissolution kinetics of alumina and silica from calcined materials

Preparation of Aluminum Hydroxide from High-alumina Fly Ash:An Experimental Study

Thermal Behavior of Pyrophyllite Ore during Calcination for Thermal Activation for Aluminum Extraction by Acid Leaching

SYNTHESIS OF MAGNESIUM-ALUMINUM MIXED OXIDE FROM HYDROTALCITE AND ITS PERFORMANCES AS CATALYTIC SUPPORT

Mechanism study of synergistic aluminum extraction and purification by ammonium for high-value conversion of secondary aluminum dross

Kinetics of the Thermal Decomposition of Aluminum Sulfate

The Promotion Mechanism Of Silicon-Aluminum On The Decomposition Of Sulfates In Biomass Ash

Study of High Temperature Phase of Sulphoaluminate for Desulfuration

Kinetics of aluminum extraction from roasting activated fly ash by sulfuric acid leaching

Experimental Study of the Pyrolysis Path of CaSO3·1/2H2O

Cooling Crystallization of Aluminum Sulfate in Pure Water Modulated by Sodium Dodecylbenzenesulfonate

High-Efficiency Desulfurization of High-Sulfur Bauxite Calcined in a Conveyor Bed: Kinetics, Process, and Application

Extraction of alumina from high-alumina fly ash by ammonium sulfate: roasting kinetics and mechanism

Mechanism and Kinetics Study of Sintering Process for Alumina Recovery from Fly Ash

Kinetic and thermodynamic analysis on preparation of belite-calcium sulphoaluminate cement using electrolytic manganese residue and barium slag by TGA