Kinetics of Carbothermal Reduction of Electric Arc Furnace Dust from a Stainless Steel Plant
Rodrigue Armel Muvunyi,Dingli Zheng,Jianli Li,Guojun Ma,Yaw Owusu-Acheaw,Xiang Zhang
DOI: https://doi.org/10.1007/s11837-022-05682-6
2023-02-13
JOM
Abstract:To optimize the stainless steel plant dust (SSD) reduction process for recovering valuable metals, a good kinetics understanding is required. In this paper, the thermodynamics of carbothermal reduction of SSD were analyzed. In addition, the non-isothermal kinetics of SSD carbothermal reduction, combined with thermogravimetric analysis, XRD, and SEM–EDS were studied by applying the Flynn–Wall–Ozawa (FWO) and Málek models. Thermodynamics and kinetic analysis results illustrate that below 950°C, the main reduction reaction is direct reduction between SSD and carbon. As the temperature increases, indirect reduction leads the reduction process of hematite due to CO formation. The reaction is highly temperature dependent and the reduction rate increases with temperature increments. The activation energy initially increased; it was 151.69 kJ/mol when the reduction rate (α) was 0.1. In the middle stage of the reaction, it slightly decreased from 343.76 kJ/mol when α ≥ 0.3, before continually increasing when α ≥ 0.6. The reduction process is a multistep reaction. The controlling step in the initial stage (α ≤ 0.2) is a shrinking core mode with the integral form 1 − (1 − α)3. As the reaction proceeds (0.2 ≤ α ≤ 0.6), the reduction is controlled by a chemical reaction expressed by (1 − α)−1 − 1. In the later stage (α ≥ 0.6), the reaction is a chemical reaction described by (1 − α)−2.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy