Modified wear behavior of selective laser melted Ti6Al4V alloy by direct current assisted ultrasonic surface rolling process

Zhen Wang,Zhongqiang Liu,Chaofeng Gao,Kaho Wong,Sujuan Ye,Zhiyu Xiao

DOI: https://doi.org/10.1016/j.surfcoat.2019.125122

IF: 4.865

2020-01-01

Surface and Coatings Technology

Abstract:Ti6Al4V alloy samples prepared by selective laser melting were treated by three different post-treatments: namely heat-treatment, ultrasonic surface rolling process (USRP) and direct current assisted ultrasonic surface rolling process (DC-USRP). Wear behaviors were evaluated using a block-on-disc rig under lubrication conditions. Results showed that the DC-USRP treated sample exhibited the lowest wear rate of 1 × 10−6 mm3 N−1 m−1, compared to that of the as-built (4 × 10−5 mm3 N−1 m−1), heat-treated (2 × 10−5 mm3 N−1 m−1) and USRP-treated samples (5 × 10−6 mm3 N−1 m−1). Consistent with changes in the wear rate, the friction coefficient was also gradually reduced. The as-built and heat-treated samples showed severe abrasive wear and delamination, while the USRP and DC-USRP treated samples displayed only mild abrasive wear. The improved wear resistance of the USRP and DC-USRP treated samples was attributed to the modified lubrication mechanism, increased hardness and compressive residual stress. Moreover, the wear resistance of the DC-USRP treated samples decreased with the increasing depth from the surface due to the effect of gradient work hardening.

physics, applied,materials science, coatings & films