Abstract:The current study is aimed to evaluate the effect of nanomaterials (nano alumina (NA) and nano silica (NS) on the mechanical and durability performance of fiber-reinforced alkali-activated mortars (FRAAM). Polypropylene fiber (PPF) was added to the binders at 0.5% and 1% of the volume of the alkali-activated mortar (AAM). Design-expert software was used to provide the central composite design (CCD) for mix proportions. This method categorizes variables into three stages. The number of mixes was created and evaluated with varied proportions of variables. The primary binders in this experiment were 50% fly ash (FA) and 50% ground granulated blast slag (GGBS). The alkali-activated solution to binder ratio was 0.5, and the sodium hydroxide (NaOH) concentration was 12 molarity. The sodium silicate to sodium hydroxide ratio was 2.5. The cubic specimens and prisms were evaluated in an ambient atmosphere at 23 + 3 °C room temperature at the ages of 7 and 28 days. The mechanical performance of AAM was indicated through evaluation of the compressive and flexural strength, flowability, and unit weight of the alkali activator mortar. In addition, the durability performance and microstructure analysis were also evaluated. The experiments demonstrated that the AAM without fibers and nanomaterials had a higher flow rate than the other mixtures. However, the flowability of all mixtures was acceptable. The highest compressive strength was deducted through the use of 2% NA and higher flexural tensile strength was obtained for mixtures included 1% NS and 0.5% PPF. The lower water absorption was noted through the combination of 2% nano silica and 1% polypropylene fiber. Whereas, the combination of 2% nano silica, 1% nano alumina, and 0.5% polypropylene fiber had the lower sorptivity. In addition, the microstructure analysis indicated that the nanomaterials significantly improved the matrix and the porosity of the matrix was considerably reduced.

Comparison of the alkali-silica reactions of ferronickel slag aggregate in fly ash geopolymer and cement mortars

Comparison of Field Observations with Laboratory Test Results on Concretes Undergoing Alkali-Silica Reaction

Potential alkali silica reaction expansion mitigation of ferronickel slag aggregate by fly ash

ASR Potential of Nickel Slag Fine Aggregate in Blast Furnace Slag-Fly Ash Geopolymer and Portland Cement Mortars

Rheology and alkali-silica reaction of alkali-activated slag mortars modified by fly ash microsphere: a comparative analysis to OPC mortars

Factors Affecting Kinetics and Gel Composition of Alkali–Silica Reaction in Alkali-Activated Slag Mortars

Influence of Cement Replacement with Fly Ash and Ground Sand with Different Fineness on Alkali-Silica Reaction of Mortar

Activator-related effects of sodium hydroxide storage solution in standard testing of fly ash geopolymer mortars for alkali–silica reaction

Alkali-silica reaction (ASR) and alkali-carbonate reaction (ACR) in activated blast furnace slag cement (ABFSC) concrete

Factors affecting compressive strength and expansion due to alkali-silica reaction of fly ash-based alkaline activated mortar

Alkali-Silica Reaction and Residual Mechanical Properties of High-Strength Mortar Containing Waste Glass Fine Aggregate and Supplementary Cementitious Materials

Alkali−Silica Activity and Inhibition Measures of Concrete Aggregate in Northwest China

Developing Geopolymer Concrete by Using Ferronickel Slag and Ground-Granulated Blast-Furnace Slag

Expansion in low calcium fly ash-based geopolymer concrete: chemical factors influenced by silica fume and NaOH concentration

Performance of Fiber-Reinforced Alkali-Activated Mortar with/without Nano Silica and Nano Alumina

ALKALI SILICA REACTION OF RECYCLED GLASS AGGREGATE MORTAR USING FLY ASH UNDER STEAM CURING

Strength and Microstructure Characteristics of Blended Fly Ash and Ground Granulated Blast Furnace Slag Geopolymer Mortars with Na and K Silicate Solution

Studies on the performance of alkali-activated aluminosilicate geopolymer mortar against exposure to acid, sulfate, and elevated temperature

Experimental study on full-volume fly ash geopolymer mortars: Sintered fly ash versus sand as fine aggregates

The Effect of Blast Furnace Slag/Fly Ash Ratio on Setting, Strength, and Shrinkage of Alkali-Activated Pastes and Concretes

Microstructure, strength development mechanism, and CO2 emission analyses of alkali-activated fly ash-slag mortars