Abstract:This work aims to explore the feasibility of self-matting coatings based on soybean oil.
What problem does this paper attempt to address?
### Problems the Paper Attempts to Solve
This paper aims to explore the feasibility of self-extinguishing coatings based on soybean oil. Specifically, the researchers synthesized a reactive waterborne polyurethane (RWPU) dispersion containing unsaturated C=C double bonds and prepared a polyurethane/acrylate (MPU) hybrid emulsion by copolymerizing with hard/soft monomers. The main objectives of the study include:
1. **Reducing Gloss**: Preparing MPU hybrid emulsions with low gloss by adjusting the ratio of hard/soft monomers.
2. **Improving Thermal Stability**: Evaluating the thermal stability of MPU-based films to ensure they maintain performance at high temperatures.
3. **Enhancing Mechanical Properties**: Testing the tensile strength and elongation at break of MPU-based films to ensure their mechanical performance in practical applications.
### Research Background
Currently, low gloss agents (also known as low gloss additives or gloss control additives) are widely used in surface coatings to reduce gloss and light reflection. These additives are commonly used in environments such as schools and hospitals to reduce visual distractions, allowing staff or students to better focus. However, traditional low gloss materials such as diatomaceous earth, silica, wax-treated silica, and clay have certain drawbacks, such as long preparation times and uneven surfaces. Therefore, there is an urgent need to develop effective, economical, and environmentally friendly low gloss materials.
Waterborne low gloss materials are favored for their low volatile organic compound (VOC) emissions. Waterborne polyurethanes (WPUs) hold an important position in existing coatings due to their lower environmental impact. Although extensive research has been devoted to developing low gloss WPU coatings, most methods still rely on petroleum-derived polyols and isocyanates, resulting in a significant environmental footprint. With the depletion of fossil fuels and increasing environmental pollution pressures, developing renewable resource materials has become a trend.
### Research Methods
1. **Raw Material Synthesis**: Using epoxidized soybean oil (ESO) as a raw material, methoxy soybean oil-based polyol (MESO) was prepared through a methanol ring-opening reaction.
2. **Synthesis of RWPU Dispersion**: MESO was reacted with isophorone diisocyanate (IPDI) and dimethylolpropionic acid (DMPA) to generate an RWPU dispersion containing unreacted isocyanate groups.
3. **Synthesis of MPU Hybrid Emulsion**: The RWPU dispersion was copolymerized with different ratios of hard/soft monomers to prepare MPU hybrid emulsions.
4. **Performance Testing**: The chemical structure, surface roughness, thermal stability, and mechanical properties of MPU-based films were characterized using FT-IR, 1H NMR, scanning electron microscopy (SEM), 3D surface profilometry, thermogravimetric analysis (TGA), particle size distribution, and ζ potential measurements.
### Main Results
1. **Low Gloss**: By adjusting the ratio of hard/soft monomers, MPU-based films with gloss as low as 3.3 gloss units were successfully prepared.
2. **Thermal Stability**: TGA results showed that MPU-based films exhibited excellent thermal stability.
3. **Mechanical Properties**: Tensile tests indicated that RWPU dispersions containing 30% hard monomers exhibited good tensile strength (13.2 MPa) and high elongation at break (578%).
4. **Storage Stability**: After one year of storage, the particle size distribution of MPU emulsions remained narrow, and the ζ potential value was around -30.0 mV, demonstrating excellent storage stability.
### Conclusion
This study successfully synthesized low gloss waterborne polyurethane/acrylate hybrid emulsions based on soybean oil, and the prepared films exhibited variable rough surfaces. The study showed that with the increase in hard monomer content, the roughness of MPU-based films increased, thermal stability improved, and gloss decreased. Therefore, by copolymerizing RWPU with an appropriate ratio of hard/soft monomers, low gloss, excellent thermal stability, and good mechanical properties can be achieved. Based on these observations, soybean oil-based polyols are considered promising candidates for synthesizing novel renewable resource-based waterborne MPUs suitable for a wide range of industrial applications.