Abstract:Plant adhesives have great potential as substitutes for formaldehyde-based adhesives due to their environmental friendliness, low cost, and nontoxicity. However, the application of this type of adhesive is challenged by its water resistance. Herein, an environmentally friendly bioadhesive was prepared from biomaterials, including waste cottonseed protein and sawdust. Isophorone diisocyanate (IPDI) and oxidized cellulose (OC) were used as double crosslinking modifiers. A protein-based bioadhesive with excellent adhesive properties and stable hydrothermal resistance was produced. The impact of IPDI and OC on the crosslinking network was evaluated by detailed Fourier transform infrared spectroscopy and X-ray photoelectron spectrometry analysis. It was found that IPDI and OC, as crosslinking agents, synergistically improved the dry and wet bonding strength of the adhesive. At the optimal loadings of 10% OC and 20% IPDI, the wet bonding strength of the adhesive reached 1.55 MPa on average, which is more than twice that of the Chinese Type II plywood adhesive standard (0.7 MPa). The dry bonding strength also increased to 2.67 MPa with this addition. The improvements in bonding strength as well as the water-resistance of the bioadhesive were ascribed to the formation of a dual-crosslinking network between the IPDI, OC, and cottonseed protein. Both protein-oxidized cellulose and protein-isophorone diisocyanate crosslinking networks were formed in the adhesive system, tightly combining the adhesive components. Thus, the biodegradable adhesive developed in this work provides an effective and convenient approach for the development of all-biomass-derived adhesives, and the constructed high-performance adhesive presents potential application for sustainable wood products.

Thermal-driven cationic waterborne polyurethane crosslinker with oxime-based and catechol structure for the preparation of soybean protein-based adhesive with excellent adhesion properties

Improving coating and prepressing performance of soy protein-based adhesive by constructing a dual-bionic topological structure

Soy protein-based adhesive with superior bonding strength and water resistance by designing densely crosslinking networks

Developing a stable high-performance soybean meal-based adhesive using a simple high-pressure homogenization technology

The bonding strength, water resistance and flame retardancy of soy protein-based adhesive by incorporating tailor-made core–shell nanohybrid compounds

Performance of soybean protein adhesive cross-linked by lignin and cuprum

Hyperbranched catechol biomineralization for preparing super antibacterial and fire-resistant soybean protein adhesives with long-term adhesion

Development of a strong and multifunctional soy protein-based adhesive with excellent coating and prepressing in wet state by constructing a radical polymerization and organic-inorganic mineralization bionic structure

Preparation and properties of soybean protein adhesive modified by chitosan/tannic-silver nanocomposite

Polyphenols induced in situ organic-inorganic crosslinking/mineralization strategy for constructing eco-friendly soy adhesive with high waterproof bonding strength

Synthesis and characterization of alkoxy silane modified polyurethane wood adhesive based on epoxidized soybean oil polyester polyol

A water-resistance soy protein-based adhesive for various substrates application by incorporating tailor-made hydrophobic nanocrystalline cellulose

Crosslinking Mechanism of Soy Protein-based Adhesives Based on Glyoxal and a Compound of Protein Model

Preparation of strong, water retention, and multifunctional soybean flour-based adhesive inspired by lobster shells and milk skin

A hair fiber inspired bio-based adhesive with high bonding strength and mildew tolerance

Tough, waterproof, and mildew-resistant fully biobased soybean protein adhesives enhanced by furfuryl alcohol with dynamic covalent linkages

A High‐Performance Bio‐Adhesive Using Hyperbranched Aminated Soybean Polysaccharide and Bio‐Based Epoxide

Cottonseed protein bioadhesive with high adhesion performance achieved by a synergistic dual-crosslinking strategy

A high-performance bio-based adhesive comprising soybean meal, silk fibroin, and tannic acid inspired by marine organisms

Preparation and Characterization of Plant Protein Adhesives with Strong Bonding Strength and Water Resistance

Preparation of a high bonding performance soybean protein-based adhesive with low crosslinker addition via microwave chemistry