Abstract:To explore the effects of freeze–thaw cycles on the mechanical properties and crack evolution of fissured sandstone, biaxial compression experiments were carried out on sandstone subjected to freeze–thaw cycles to characterize the changes in the physical and mechanical properties of fissured sandstone caused by freeze–thaw cycles. The crack evolution and crack change process on the surface of the fissured sandstone were recorded and analysed in detail via digital image technology (DIC). Numerical simulation was used to reveal the expansion process and damage mode of fine-scale cracks under the action of freeze–thaw cycles, and the simulation results were compared and analysed with the experimental data to verify the reliability of the numerical model. The results show that the mass loss, porosity, peak stress and elastic modulus all increase with increasing number of freeze–thaw cycles. With an increase in the number of freeze–thaw cycles, a substantial change in displacement occurs around the prefabricated cracks, and a stress concentration appears at the crack tip. As new cracks continue to sprout at the tips of the prefabricated cracks until the microcracks gradually penetrate into the main cracks, the displacement cloud becomes obviously discontinuous, and the contours of the displacement field in the crack fracture damage area simply intersect with the prefabricated cracks to form an obvious fracture. The damage patterns of the fractured sandstone after freeze–thaw cycles clearly differ, forming a symmetrical "L"-shaped damage pattern at zero freeze–thaw cycles, a symmetrical "V"-shaped damage pattern at 10 freeze–thaw cycles, and a "V"-shaped damage pattern at 20 freeze–thaw cycles. After 20 freeze–thaw cycles, a "V"-shaped destruction pattern and "L"-shaped destruction pattern are formed; after 30 freeze–thaw cycles, an "N"-shaped destruction pattern is formed. This shows that the failure mode of fractured sandstone gradually becomes more complicated with an increasing number of freeze–thaw cycles. The effects of freeze–thaw cycles on the direction and rate of crack propagation are revealed through a temperature–load coupled model, which provides an important reference for an in-depth understanding of the freeze–thaw failure mechanisms of fractured rock masses.

Effect of freezing temperature and number of freeze–thaw cycles on mode I and mode II fracture toughness of sandstone

Effect of freeze–thaw cycle on physical and mechanical properties and damage characteristics of sandstone

On the decay of fracture toughness of sandstone subjected to freeze–thaw cycles

Experimental study on effect of freeze-thaw cycles on dynamic mode-Ι fracture properties and microscopic damage evolution of sandstone

Experimental Investigation on Fracture Behavior and Mechanical Properties of Red Sandstone Subjected to Freeze–Thaw Cycles

Study on the microscopic damage evolution and dynamic fracture properties of sandstone under freeze-thaw cycles

Fracture mechanical properties of sandstone with pre-fabricated cracks under freeze–thaw cycles

Fracture behavior of yellow sandstone under freeze–thaw cycles with varied saturation states: An investigation of mode I fracture

Surface crack evolution patterns in freeze-thaw damage of fissured rock bodies

Damage mechanism of sandstones subject to cyclic freeze–thaw (FT) actions based on high-resolution computed tomography (CT)

Mechanical characteristics and freeze–thaw damage mechanisms of mode-I cracked sandstone from the Three Gorges Reservoir region under different chemical solutions

Study on the mechanical properties of saturated red sandstone under freeze–thaw conditions

Damage characteristics of sandstone pore structure under freeze-thaw cycles

Assessing the effect of freezing-thawing cycles on the results of the triaxial compressive strength test for calc-schist rock

Quantitative Study of the Failure Characteristics of Sandstone with Freeze–Thaw Damage: Insight into the Cracking Behavior

Influence of Microstructure on Dynamic Mechanical Behavior and Damage Evolution of Frozen-Thawed Sandstone Using Computed Tomography

Damage and failure characteristics of single fractured cyan sandstone subjected to freeze–thaw cycles under uniaxial compression

Research on triaxial compressive mechanical properties and damage constructive model of post-thawing double-fractured quasi-sandstones with different angles

Effects of cyclic freezing and thawing on the mechanical behavior of dried and saturated sandstone

Mechanical Characteristics of Red Sandstone Subjected to Freeze–Thaw Cycles and Increasing Amplitude Cyclic Load

Deterioration of dynamic fracture characteristics, tensile strength and elastic modulus of tight sandstone under dry-wet cycles