Abstract:In present study, a layer of continuous and compact graphene coating was deposited on the surface of microcrystalline diamond (MCD) and nanocrystalline diamond (NCD) film by electrophoretic deposition (EPD) method. The tribological performance of as-deposited films, referred as Gr/MCD and Gr/NCD respectively, was investigated in a set of ball-on-plate reciprocating friction tests in ambient atmosphere (60% RH). Under a normal load of 4N (corresponding to a contact pressure of 770MPa), the stable COF of Gr/MCD film reduced by 60% compared with that of MCD film, which decreased from 0.166 to 0.068; in contrast, the stable COF of Gr/NCD film was comparable with that of NCD film, which were measured as 0.069 and 0.074 respectively. For the Gr/MCD film, the unique surface morphology of underneath MCD film was supposed to play a crucial role on its exceptional friction performance. It produced a plenty of wear particles during the run-in sliding stage and a large portion of these particles were trapped in the sliding interface. During the following stable sliding stage, graphene scrolls formed by graphene sheets wrapping around the wear particles they encountered and attributed to the reduction in friction by decreasing the interfacial contact area and forming an incommensurable contact between the graphene scrolls and counterpart surface. For the Gr/NCD film, in contrast, the absence of wear particles on its sliding interface and structural degradation in its top-layered graphene sheets was supposed to result in its failure in reducing friction. Different from the Gr/MCD film, the residual graphene flakes on the worn surface of Gr/NCD film were transformed to disordered graphitic structures; meanwhile, increased defects and severe oxidation effect were detected in them. Furthermore, due to the exceptional protection effect of graphene coating, the Gr/MCD and Gr/NCD film produced severer wear on the counterface than the MCD and NCD film.

Effect of airborne contaminants on the macroscopic anti-wear performance of chemical vapor deposition graphene

Wear Evolution of Monolayer Graphene at the Macroscale

Electric Resistance As a Sensitive Measure for Detecting Graphene Wear During Macroscale Tribological Tests

Suppressing Nanoscale Wear by Graphene/Graphene Interfacial Contact Architecture: A Molecular Dynamics Study.

First-Principles Study of the Friction and Wear Resistance of Graphene Sheets

Environmental Molecular Effect on the Macroscale Friction Behaviors of Graphene

Graphene Failure under MPa: Nanowear of Step Edges Initiated by Interfacial Mechanochemical Reactions

Effect of Humidity on the Wear Behavior of Graphene under Current Carrying Conditions

Macroscale Superlubricity and Durability of in Situ Grown Hydrogenated Graphene Coatings

Impacts of environments on nanoscale wear behavior of graphene: Edge passivation vs. substrate pinning

The role of oxygen in mechanochemical wear of graphene

Nanoscale Mechanism of Suppression of Friction and Wear of the Diamond Substrate by Graphene

Effects of Grain Boundary on Wear of Graphene at the Nanoscale: A Molecular Dynamics Study

Impacts of the Substrate Stiffness on the Anti-Wear Performance of Graphene

The Impacts of Adhesion on the Wear Property of Graphene

Mechanochemical functionality of graphene additives in ultralow wear polytetrafluoroethylene composites

Wear Resistance Limited by Step Edge Failure: the Rise and Fall of Graphene As an Atomically Thin Lubricating Material.

Structure, superlubricity, applications, and chemical vapor deposition methods of graphene solid lubricants

Synergistic Friction-Reducing and Anti-Wear Behaviors of Graphene with Micro- and Nano-Crystalline Diamond Films

Effects of Thickness and Particle Size on Tribological Properties of Graphene as Lubricant Additive

Macroscale, Humidity-Insensitive, and Stable Structural Superlubricity Achieved with Hydrogen-Free Graphene Nanoflakes